Colloidal electrolyte accumulator and production method

A technology of colloidal electrolyte and manufacturing method, which is applied in the direction of lead-acid batteries, electric vehicles, vehicle energy storage, etc., can solve the problems of unstable performance, small starting current, and low capacity, and achieve low cost, improved manufacturing method, and storage capacity big effect

Inactive Publication Date: 2011-06-29
杨建平 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above problems of unstable performance, large internal resistance, small instantaneous starting current, and low capacity, the purpose of the present invention is to provide a colloidal electrolyte battery with stable performance, large capacity and good starting performance; another purpose of the present invention is In order to provide a manufacturing method of the storage battery

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The colloidal electrolyte of the colloidal electrolyte battery contains the following components, and its weight percentage is: sulfuric acid 35%, silicon 2%, phosphoric acid 1%, polyacrylamide 1%, ethylene glycol 0.1%, propionic acid alcohol 1%, potassium 0.01%, ammonium 0.01%, germanium 0.01%, cadmium 0.06%, lithium 0.008%, and the rest is water.

[0024] The manufacturing method of gel electrolyte battery is as follows:

[0025] The first step: preparing the components of the above-mentioned colloidal electrolyte into materials A and B;

[0026] Wherein, the preparation method of material A is:

[0027] 1. Dilute concentrated sulfuric acid with water to a density of 1.48g / cm 3 , after multi-stage filtering;

[0028] 2. Add phosphoric acid, cadmium, germanium, and ammonium into the diluted sulfuric acid, and stir evenly;

[0029] The preparation method of material B is:

[0030] 1. Dilute industrial sodium silicate with water to a density of 1.01g / cm 3 , precipi...

Embodiment 2

[0036] The colloidal electrolyte of the colloidal electrolyte battery contains the following components, and its weight percentage is: sulfuric acid 42%, silicon 10%, phosphoric acid 5%, polyacrylamide 5%, ethylene glycol 0.5%, propionic acid alcohol 5%, potassium 0.02%, ammonium 0.02%, germanium 0.02%, cadmium 0.1%, lithium 0.01%, and the rest is water.

[0037] The manufacturing method of gel electrolyte battery is as follows:

[0038] The first step: preparing the components of the above-mentioned colloidal electrolyte into materials A and B;

[0039] Wherein, the preparation method of material A is:

[0040] 1. Dilute concentrated sulfuric acid with water to a density of 1.48g / cm 3 , after multi-stage filtering;

[0041] 2. Add phosphoric acid, cadmium, germanium, and ammonium into the diluted sulfuric acid, and stir evenly;

[0042] The preparation method of material B is:

[0043] 1. Dilute industrial sodium silicate with water to a density of 1.01g / cm 3 , precipit...

Embodiment 3

[0049] The colloidal electrolyte of the colloidal electrolyte battery contains the following components, and its weight percentage is: sulfuric acid 40%, silicon 8%, phosphoric acid 3%, polyacrylamide 3%, ethylene glycol 0.3%, propionic acid alcohol 3%, potassium 0.01%, ammonium 0.01%, germanium 0.01%, cadmium 0.05%, lithium 0.005%, and the rest is water.

[0050] The manufacturing method of gel electrolyte battery is as follows:

[0051]The first step: preparing the components of the above-mentioned colloidal electrolyte into materials A and B;

[0052] Wherein, the preparation method of material A is:

[0053] 1. Dilute concentrated sulfuric acid with water to a density of 1.48g / cm 3 , after multi-stage filtering;

[0054] 2. Add phosphoric acid, cadmium, germanium, and ammonium into the diluted sulfuric acid, and stir evenly;

[0055] The preparation method of material B is:

[0056] 1. Dilute industrial sodium silicate with water to a density of 1.01g / cm 3 , precipit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a colloid electrolyte accumulator which includes components by weight percent of: 35-42 of sulfuric acid, 2-10 of silicon, 1-5 of phosphoric acid, 1-5 of polyacrylamide, 0.1-0.5 of glycol, 1-5 of propionyloxy alcohol, 0.01-0.02 of potassium, 0.01-0.02 of ammonium, 0.01-0.02 of germanium, 0.06-0.1 of cadmium, 0.008-0.01 of lithium, and the balance of water. The invention also relates to a preparation method of the accumulator. The colloid electrolyte accumulator has low cost, high storage capacity, strong starting capability at low temperature and can be applied in field of automobile, electric vehicle, beacon light, emergency power source and so on.

Description

technical field [0001] The invention relates to the technical field of storage batteries, in particular to a colloidal electrolyte storage battery, and also relates to a manufacturing method of the colloidal electrolyte storage battery. Background technique [0002] In the prior art, the batteries currently used are still mainly ordinary lead-acid batteries, because the configuration method is simple and the cost is low. However, when lead-acid batteries use lead-acid electrolytes during charging or leakage, etc., acid mist is precipitated, which is harmful to human health and pollutes the environment; lead-acid electrolytes are corrosive and will corrode equipment; and because lead-acid electrolytes have Volatility will cause the active material and acid reaction ability of the positive and negative plates to decrease, resulting in short storage period when charged, serious self-discharge and other problems. [0003] In order to adapt to higher environmental protection req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/10H01M10/08
CPCY02T10/7016Y02E60/126Y02E60/10
Inventor 杨建平杨胜
Owner 杨建平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap