Initial magnetic-inductive capacity 40 (-8) (+8) nickel-zinc ferrite material and preparation method

A nickel-zinc ferrite, initial permeability technology, applied in the direction of inorganic material magnetism, etc., can solve the problems of rising eddy current loss of ferrite, increase production cost, reduce lamp efficiency, etc., achieve good temperature characteristics, broadband and low electromagnetic loss, the effect of good electromagnetic loss characteristics

Inactive Publication Date: 2008-10-15
TONGXIANG TELIYOU ELECTRONICS SCI & TECH
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, 3F4 power manganese zinc ferrite is generally used abroad to prepare power couplers in high frequency electrodeless lamps, but due to the existence of Fe 2 + ⇔ Fe 3 + Such a conductive pair, so its resistivity is usually low, and because the operating frequency of the high-frequency electrodeless lamp is usually above 2MHz, this leads to a sharp inc...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Initial magnetic-inductive capacity 40 (-8) (+8) nickel-zinc ferrite material and preparation method
  • Initial magnetic-inductive capacity 40 (-8) (+8) nickel-zinc ferrite material and preparation method
  • Initial magnetic-inductive capacity 40 (-8) (+8) nickel-zinc ferrite material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1) Selection of raw materials: a kind of nickel-zinc ferrite material with an initial magnetic permeability of 46 and its preparation method provided in this embodiment, its raw material selects industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0033] 2) Composition design and weighing: according to Fe 2 o 3 49mol%, ZnO 8mol%, MnCO 3 1 mol%, NiO 41.7 mol%, and CoO 0.3 mol%.

[0034] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 2 hours.

[0035] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 950°C, and the pre-burning time is 3.5 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed that...

Embodiment 2

[0043] 1) Selection of raw material: a kind of nickel-zinc ferrite material and preparation method with an initial magnetic permeability of 39 provided in this embodiment, its raw material selects industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0044] 2) Composition design and weighing: according to Fe 2 o 3 46mol%, ZnO 4.4mol%, MnCO 3 0.1 mol%, NiO 48 mol%, and CoO 1.5 mol%.

[0045] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 1 hour.

[0046] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 1100°C, and the pre-burning time is 1.5 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed that on...

Embodiment 3

[0054] 1) Selection of raw material: a kind of nickel-zinc ferrite material and preparation method with an initial magnetic permeability of 34 provided in this embodiment, its raw material selects industrially pure Fe 2 o 3 , ZnO, MnCO 3 , NiO and CoO.

[0055] 2) Composition design and weighing: according to Fe 2 o 3 49mol%, ZnO 2mol%, MnCO 3 0.4 mol%, NiO 48 mol%, and CoO 0.6 mol%.

[0056] 3) Mixing of raw materials: Put the weighed raw materials into a sand mill, add deionized water, the weight of deionized water is 1.2 times of the total weight of raw materials, and the ball milling time is 1.5 hours.

[0057] 4) Pre-burning: Dry the raw materials that have been ball-milled once, and put them into an electric furnace for pre-burning. The pre-burning temperature is 1000°C, and the pre-burning time is 2 hours. After pre-burning, it is cooled with the furnace. After pre-burning, XRD phase analysis was carried out on the pre-fired material, and it was confirmed that onl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Average particle sizeaaaaaaaaaa
Saturation flux densityaaaaaaaaaa
Curie temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses an oxygen body material of nickel, zinc and ferrum with initial permeability being 40<-8><+8> and a preparation method thereof. The main phase of the material is spinel structure, and the material essentially consists of Fe2O3, ZnO, MnO, NiO and CoO, and the contents of composition calculated by oxide are: 46mol percent to 49mol percent of Fe2O3, 2mol percent to 8mol percent of ZnO, 0.1mol percent to 1.0mol percent of MnO, 41.7mol percent to 48mol percent of NiO and 0.3mol percent to 1.5mol percent of CoO; the oxygen body material of nickel, zinc and ferrum with initial permeability being 40<-8><+8> has broadband, low electromagnetic consumption and good stability in larger working current and can be used for producing various power couplers of high-frequency electrodeless lamps with the working frequency in 30MHz; the material has extremely low electromagnetic consumption in high frequency ranging from 2MHz to 30MHz; when the frequency is in the range of 2.5MHz to 3MHz, the quality factor Q is more than 200; when the frequency is 30MHz, the quality factor Q is more than 80; due to good electromagnetic consumption characteristic in such wide frequency range, the oxygen body material can be applied to any electrodeless lamp with the working frequency in 30MHz.

Description

technical field [0001] The invention relates to a nickel-zinc ferrite material that can be used to make power couplers for various high-frequency electrodeless lamps with an operating frequency within 30 MHz, especially a nickel-zinc ferrite material with an initial magnetic permeability of 40 -8 +8 Nickel zinc ferrite material and preparation method thereof. Background technique [0002] High Frequency Electronic Discharge Lamp (High Frequency Electronic Discharge Lamp) is a high-tech new light source that integrates the latest electronic power-saving technology and electric light source technology. It does not use a filament, but uses a magnetic field to stimulate gas discharge and light emission. It is highly efficient, energy-saving, and environmentally friendly. , long life and many other advantages. The high-frequency electrodeless lamp is composed of three parts: the excitation power supply, the power coupler and the bulb. The excitation source generates an electric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F1/11C04B35/26C04B35/622B22F9/04
Inventor 胡军顾晔华
Owner TONGXIANG TELIYOU ELECTRONICS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap