Anti-fouling anti-dazzle film

An anti-glare film and anti-fouling technology, applied in optics, optical components, instruments, etc., can solve the problems of glare glare, easy scratches on the touch panel surface, sticking, etc., to improve water resistance, avoid whitening, The effect of improving wettability

Active Publication Date: 2010-06-02
CHINA LUCKY FILM CORP
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During daily use, the problems that are often encountered are: (1) the surface of the touch panel is easily scratched; (2) the surface of the touch panel is easily stained by fingerprints, water vapor, dust, etc.; (3) the "glare" caused by external light on the surface Dazzling"
The above-mentioned technology can only be used to suppress the adhesion of materials used in daily life such as food and cosmetics, and can easily remove these materials
The disadvantage of conventional stain-resistant anti-glare films is that fingerprints will adhere to the film after input operations with fingers, and the attached fingerprints are not easily wiped off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-fouling anti-dazzle film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] 50 parts of dipentaerythritol penta- and hexaacrylates;

[0045] BYK-486 1.5 copies;

[0046] Silica particles (model 720) 3.0 parts;

[0047] Irgacure 1173 6.0 parts;

[0048] Butanone 20 parts;

[0049] 20 parts of isopropanol.

[0050] In 50 parts by weight of dipentaerythritol penta- and hexaacrylate (DPHA, Nippon Kayaku) (solid component concentration: 100%), add 1.5 parts by weight of organosilicon-modified polyacrylate BYK-486 ( German BYK company), while adding 3.0 parts by weight of silicon dioxide particles (German Degussa company, model 720) with an average particle diameter of 3.0 microns. Dilute the above mixture with a mixed solvent of 20 parts of methyl ethyl ketone and 20 parts of isopropanol, carry out high-shear dispersion for 30 minutes, add 4 parts by weight of photoinitiator Irgacure 1173 (Nanjing Jiean Chemical Co., Ltd.) after dispersion, and obtain a coating cloth liquid.

[0051] The resulting coating liquid was applied to one side of a po...

Embodiment 2

[0053] Three, 30 parts of pentaerythritol tetra(meth)acrylates;

[0054] BYK 436 0.8 parts;

[0055] 1.5 parts of silicon dioxide particles (model 720);

[0056] 184 5 copies;

[0057] Butanone 33 parts;

[0058] Ethyl Cellosolve 30 parts.

[0059] In 30 parts by weight of three and tetra(meth)acrylate pentaerythritol esters (Yixing Honghui Chemical Co., Ltd.), add 0.8 parts by weight of organosilicon-modified polyacrylate BYK-486 (Germany BYK) containing hydroxyl functional groups , while adding 1.5 parts by weight of silicon dioxide particles with an average particle size of 3.0 microns (Degussa, Germany, model 720). Dilute the above mixture with a mixed solvent of 33 parts of methyl ethyl ketone and 30 parts of ethyl cellosolve, carry out high-shear dispersion for 50 minutes, add 5 parts by weight of photoinitiator 184 (Changzhou Huatai Company) after dispersion, and obtain a coating solution .

[0060] The resulting coating liquid was applied to one side of a polyeth...

Embodiment 3

[0062] 35 parts of dipentaerythritol penta- and hexaacrylates;

[0063] 30 parts of polyurethane acrylate;

[0064] BYK 486 1.5 copies;

[0065] Silica particles (Jinyuan 3#) 2.5 parts;

[0066] Irgacure 1173 6.0 parts;

[0067] Butanone 13 parts;

[0068] 13 parts of isopropanol.

[0069] To 35 parts by weight of dipentaerythritol penta- and hexaacrylates and 30 parts by weight of urethane acrylates, add 1.5 parts by weight of organosilicon-modified polyacrylate BYK-486 containing hydroxyl functional groups, and add 2.5 parts by weight, average particle size The 5.6-micron silicon dioxide particle Jinyuan 3# (manufactured by Tianjin Research Institute of Chemical Industry). The above mixture was diluted with a mixed solvent of 13 parts of methyl ethyl ketone and 13 parts of isopropanol, and subjected to high-shear dispersion for 40 minutes. After dispersion, 6 parts by weight of photoinitiator Irgacure 1173 was added to obtain a coating liquid.

[0070] The resulting co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
contact angleaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A dirt resistant anti-dazzle film comprises a transparent supporter and an anti-dazzle hard coating. The component and content of the anti-dazzle hard coating are as follows when counted by weight: 15-85 parts of ultraviolet solidified resin; 1-15 parts of photoinitiator; 0.1-10 parts of organsilicon modified polyacrylate; 0.5-10 parts of anti-dazzle particles, and 15-80 parts of dissolvent. The scratchproof anti-dazzle film can effectively inhibit the adhesion of dirt of dust, oil dust and the like on the surface of the film, and furthermore the adhered dirt can be easily erased. In particular the dirt resistance is permanent, and at the same time the anti-dazzle property, scratch resistance and scratchproof quality can be maintained.

Description

technical field [0001] The present invention relates to an anti-glare film with anti-fouling properties for display devices. Background technique [0002] So far, anti-glare film is mainly used for the protection of the surface and to prevent glare in various image display devices such as LCD (liquid crystal display), touch panel, CRT (cathode ray tube), PDP (plasma display panel), EL (field effect luminescent monitors) and glare and reflections in optical discs. [0003] Touch panels are used as input means for portable information terminal devices that have been widely used in recent years. The touch panel is a device for inputting data by directly touching the surface of the display with a finger or a pen, and about 90% of the entire touch panel is a resistant film type touch panel. During daily use, the problems that are often encountered are: (1) the surface of the touch panel is easily scratched; (2) the surface of the touch panel is easily stained by fingerprints, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B1/10C09D4/02G02B1/14
Inventor 王志坚于佩强
Owner CHINA LUCKY FILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com