Modified PP-R material

A PP-R, modified technology, applied in the field of plastic materials, can solve harsh problems

Active Publication Date: 2008-12-03
浙江爱康实业有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the continuous development of society, the harsh construction conditions on site and the continuous im

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] PP-R content is 97%wt, dicumyl peroxide is 3%wt. The modified PP-R pipe is extruded by blending method.

Embodiment 2

[0012] PP-R content is 95%wt, dicumyl peroxide is 5%wt. All the other are with embodiment 1.

Embodiment 3

[0014] PP-R content is 90%wt, dicumyl peroxide is 10%wt. All the other are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a modified PP-R material for reducing low-temperature brittleness of PP-R and improving rigidity of PP-R material without influencing the toughness. The modified PP-R material comprises PP-R and dicumyl peroxide and is characterized in that the modified PP-R material contains 90 to 97wt percent of PP-R and 3 to 10wt percent of dicumyl peroxide. In the modified PP-R material, micro-cross-linking technology is utilized to influence the sequence structure of random polymer as well as the sequence structure of homo-polymerization section, so that the isotactic structure of PP main chain is reduced to influence the regularity of the chain and enhance the randomness of the main chain, thus enhancing the rigidity of PP-R and improving the mechanical strength of PP-R. Because the dicumyl peroxide belongs to thermoplastic material, the modified PP-R is recoverable and environment-friendly, and causes no pollution to the environment.

Description

technical field [0001] The present invention generally relates to a plastic material, in particular to a modified PP-R material. Background technique [0002] As the country formulates the policy of "replacing steel with plastic" and building an energy-saving society, plastic pipes are widely used in more and more areas, among which PP-R pipes are more widely used. [0003] PP-R pipe has the advantages of corrosion resistance, small friction coefficient, good flexibility, small bending radius, good temperature and pressure resistance, etc., and has been applied in the fields of water supply and heating. However, with the continuous development of society, the harsh construction conditions on site and the continuous improvement of use requirements, relying on the original characteristics of PP-R can no longer meet the current needs. This is mainly manifested in the fact that PP-R pipes show brittleness under low temperature conditions, and because PP-R itself has a certain d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08K5/14
Inventor 郑立克
Owner 浙江爱康实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products