Highly water-resistant, wearing-resistant plastic printing ink and use method thereof

A technology of plastic ink and wear resistance, applied in the field of ink, can solve the problems of reducing production cost, ink fading, etc., and achieve the effect of reduced equipment investment, strong adhesion, and full color of printed products

Inactive Publication Date: 2010-12-08
NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the deficiencies in the prior art, the present invention proposes a plastic ink with water resistance and wear resistance, which can meet the requirements of water resistance and wear resistance of printed matter without coating and glazing treatment, solve the problem of ink fading, and reduce production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Component A comprises by following parts by weight:

[0028] Everlasting Red 8

[0029] Ternary resin containing hydroxychloride 15

[0030] Hydroxyl Fluorosilicone 4

[0031] Ethyl acetate 30

[0032] Propyl acetate 42

[0033] Polyethylene wax 1

[0034] Weigh 80 grams of Everlasting Red, 150 grams of hydroxychloroacetic acid ternary resin, 40 grams of hydroxyfluorosilicone resin and 10 grams of polyethylene wax. Disperse and dissolve the hydroxychloride-containing ternary resin and the hydroxy-containing fluorosilicone resin in a mixed solvent composed of 300 grams of ethyl acetate and 420 grams of propyl acetate with a high-speed disperser at room temperature at a speed of 800 rpm to make a resin solution . At the same dispersion speed, add permanent red and polyethylene wax to the resin solution in sequence, and continue to disperse evenly. The dispersed solution is ground in a closed sand mill until the fineness reaches below 20 microns, and finally filtere...

Embodiment 2

[0041] Component A comprises by following parts by weight:

[0042] Phthalocyanine blue 10

[0043] Ternary resin containing hydroxychloride 20

[0044] Hydroxyl Fluorosilicone 5

[0045]Ethyl acetate 30

[0046] Propyl acetate 44

[0047] Polyethylene wax 1

[0048] The high water and abrasion resistance plastic ink comprises by following parts by weight:

[0049] Component A 75

[0050] Component B (hexamethylene diisocyanate biuret) 8

[0051] Ethyl acetate 25

[0052] The preparation process of component A and high water-resistant and wear-resistant plastic ink is the same as that of Example 1.

Embodiment 3

[0054] Component A comprises by following parts by weight:

[0055] Benzidine Yellow 5

[0056] Ternary resin containing hydroxychloride 13

[0057] Hydroxyl Fluorosilicone 3

[0058] Ethyl acetate 25

[0059] Propyl acetate 42

[0060] Polyethylene wax 0.5

[0061] The high water and abrasion resistance plastic ink comprises by following parts by weight:

[0062] Component A 65

[0063] Component B (hexamethylene diisocyanate biuret) 5

[0064] Ethyl acetate 20

[0065] The preparation process of A component and high water and abrasion resistance plastic ink is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Highly hydrostable abrasion resistant plastic printing ink is characterized in that: the printing ink comprises the following compositions in weight portion: 65 to 75 portions of a composition A and 5 to 10 portions of a composition B of a curing agent; the composition A comprises pigment, a bonding material and a solvent, wherein the bonding material is tribasic vinyl chloride-acetate copolymer containing hydroxyl groups and a fluoro-siloxane resin containing the hydroxyl groups; and the curing agent is hexamethylene diisocyanate biuret. An application method comprises the following steps of: separately storing the composition A and the composition B; before use, diluting the composition B with a solvent, and then adding the composition B into the composition A for even mixing and dispersing; carrying out the corona treatment on a plastic film before printing to improve the surface tension of the film, up to more than 38 dynes; and carrying out curing for 12 to 24 hours in an oven ata temperature of between 40 and 70 DEG C after printing. The invention is mainly used for making the printing ink.

Description

technical field [0001] The present invention relates to printing ink, especially to a kind of plastic printing ink with high water resistance and abrasion resistance Background technique [0002] Plastic films such as polyethylene (PE) and polypropylene (PP) are the most commonly used plastic films for flexible packaging. They are non-polar materials with a compact, smooth surface and relatively low surface energy. They are an inert surface that is not easy to infiltrate and adhere. higher technical requirements. In particular, plastic inks used in the outer packaging of refrigerated products such as liquid dairy products need to meet the requirements of water resistance and abrasion resistance. , Due to the alternation of cold and heat on the surface of the film, condensation will occur. During the entire storage, transportation and use process, it is inevitable to contact with water. If the water resistance and wear resistance are poor, it is easy to cause the ink to fad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/10B41M1/30C09D11/00
Inventor 彭丹律微波孟宪铎李金辉萧潇
Owner NEW MATERIAL INST OF SHANDONG ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap