High-temperature solder for welding TiAl group alloy and preparation method thereof

A technology of high-temperature brazing filler metal and base alloy, applied in welding equipment, metal processing equipment, welding/cutting medium/material, etc., can solve the problems of limited applicable joint forms, complicated brazing filler metal preparation process, and expensive brazing filler metal, etc. To achieve the effect of improving the melting and wetting ability, good wettability and suitable melting point

Inactive Publication Date: 2010-07-14
HARBIN INST OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the problems of low strength of TiAl-based alloy brazing joints under high temperature environment, high price of brazing materials used, limited applicable joint forms and complex preparation process of brazing materials, and proposes a method applicable to various forms. Joint requirements, low production cost, simple preparation process, good strength of brazed joints under high temperature environment, titanium-based powder filler metal for brazing TiAl-based alloys and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature solder for welding TiAl group alloy and preparation method thereof
  • High-temperature solder for welding TiAl group alloy and preparation method thereof
  • High-temperature solder for welding TiAl group alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0014] Specific Embodiment 1: The high-temperature brazing filler metal used for TiAl-based alloy brazing according to this embodiment is composed of 68% to 71.7% TiH 2 , 28% to 31.7% of Ni, 0.2% to 0.5% of Si and 0.1% to 0.3% of C.

[0015] TiH in this embodiment 2 The powder mass purity is 90%-99.9%.

specific Embodiment approach 2

[0016] Specific embodiment two: the difference between this embodiment and specific embodiment one is that the high-temperature brazing filler metal used for TiAl-based alloy brazing consists of 69.6% TiH according to the weight percentage 2 , 30% Ni, 0.2% Si and 0.2% C. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0017] Specific embodiment three: the difference between this embodiment and specific embodiment one is that the high-temperature brazing filler metal used for TiAl-based alloy brazing consists of 69.3% TiH according to the weight percentage 2 , 30% Ni, 0.5% Si and 0.2% C. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature brazing filler metal used for TiAl-based alloy braze welding, and a preparation method thereof, relates to a brazing filler metal and a preparation method thereof, and solves the problems that the strength of a TiAl-based alloy braze welding joint is low in a high-temperature environment, the price of the brazing filler metal is high, the forms of adaptable joints are restricted, and the production process of the brazing filler metal is complicated. The brazing filler metal is made from TiH2, Ni, Si and C according to certain weight percentage by twosteps, namely material preparation and mechanical alloying. For TiAl-based alloy, the melting point of the brazing filler metal is appropriate, the wetting property is good, the cost is low, the braze welding quality is good, the braze welding joint has good high-temperature mechanical properties, and the requirements of various types of joints are satisfied; moreover, the production process and equipment for the brazing filler metal are simple, and the production efficiency is high.

Description

technical field [0001] The invention relates to a brazing material and a preparation method thereof. Background technique [0002] TiAl-based alloys have a low density (about 3.8g / cm 3 ), high specific strength, good rigidity, and good high-temperature mechanical properties are considered to be an ideal new type of high-temperature-resistant material, and have broad application prospects in aviation, aerospace, automotive and other fields. However, the application of TiAl-based alloys in engineering to make components must involve welding problems, including its own welding and welding of other materials. Scholars at home and abroad have conducted relevant research on the welding of TiAl-based alloys. According to current literature and related reports, TiAl-based alloys have high melting points and high hardness. Their weldability shows that using brazing methods to join TiAl-based alloys is a more suitable method. [0003] But now also there are following problems in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/24B02C17/16
Inventor 何鹏曹健王明冯吉才范龙
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com