Wet zinc metallurgical ultrasound purification method, device and use

A purification device and wet method technology, which is applied in the field of wet method zinc metallurgy purification, can solve the problems of unfavorable ultrasonic strengthening effect, unsatisfactory industrialization effect, and insufficient stability of ultrasonic irradiation effect, and achieve the effect of improving stability

Inactive Publication Date: 2011-11-09
XINGMIN TECH ZHUZHOU
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] But at the same time, it is also found that the purification method of "one-pot cooking" proposed by this patent is not stable enough for ultrasonic irradiation, which is not conducive to giving full play to the strengthening effect of ultrasonic waves, so that the industrialization effect is not ideal when the laboratory effect is good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wet zinc metallurgical ultrasound purification method, device and use
  • Wet zinc metallurgical ultrasound purification method, device and use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] pass figure 1 It can be seen that the present invention is an ultrasonic purification method for wet zinc metallurgy. In the ultrasonic purification device for wet zinc metallurgy, the ultrasonic sound field generated by ultrasonic waves is used to perform irreversible ultrasonic irradiation on the wet zinc metallurgy solution to be purified, so that the liquid after the purification reaction The concentration of ionic impurity tends to decrease irreversibly, so as to achieve the purpose of impurity removal. The ultrasonic sound field at least includes a frequency of 15-28kHz and a sound intensity of 0.5-5w / cm 2 ultrasonic sound field. The hydrometallurgical solution to be purified is the solution after leaching of zinc ore powder containing copper, cadmium, cobalt, and nickel ionic impurities (commonly known as the supernatant), and the concentration range of the ionic impurities includes at least: copper ≤2000mg / L and (or) cadmium ≤2000mg / L and (or) cobalt ≤200mg / L ...

Embodiment 2

[0040] figure 1 For another embodiment of the present invention, from figure 1 It can be seen that the present invention is an ultrasonic purification device for realizing the ultrasonic purification method of wet zinc metallurgy.

[0041] The ultrasonic purification device for wet zinc metallurgy includes at least one ultrasonic purification reaction chamber 3 filled with the solution 1 to be purified. The ultrasonic purification reaction chamber can be open at the top and vertically cylindrical or positive at the top. The combination cavity is polygonal cylindrical and the lower part is converging downward, and is provided with an inlet 2 for the solution to be purified, an outlet 7 for the liquid after the ultrasonic purification reaction, and a bottom outflow port 18 for the liquid after the ultrasonic purification reaction. In the middle of the ultrasonic purification reaction chamber, there is an ultrasonic sound field with a frequency of 15kHz and a sound intensity of ...

Embodiment 3

[0046] Conventional supernatant ultrasonic purification process for producing total slag of copper, cadmium, cobalt and nickel: two-stage ultrasonic purification process.

[0047] The first-stage ultrasonic purification process: remove copper, cadmium, cobalt and nickel, and produce total slag of copper, cadmium, cobalt and nickel.

[0048] The purification temperature is 70-85°C, and the ultrasonic purification time is 5 minutes. Among them, the purification time of irreversible ultrasonic irradiation area A is 2 minutes, and the purification time of irreversible ultrasonic irradiation area B is 3 minutes.

[0049] The solution to be purified at 70-85°C enters the mixing tank first, and the amount of zinc powder corresponding to the content of ionic impurities copper + cadmium in the solution to be purified is 1:1-1.5, the amount of zinc powder corresponding to the content of cobalt 1:20-100, and the content of nickel The amount of zinc powder corresponding to 1:20-50 is add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an ultrasonic purification method for wet zinc smelting, and a device and application thereof. In the ultrasonic purification device for wet zinc smelting, an ultrasonic field produced by ultrasonic waves is adopted to carry out irreversible ultrasonic irradiation to wet zinc smelting solution to be purified, which causes the concentration of ionic impurities to be decreased irreversibly so as to realize the purpose of removing impurities. The application of the method can realize quick purification of required standards, greatly decreases the consumption of zinc powder, directly produces high-quality copper residue, cadmium residue and cobalt residue, and also is applicable to the treatment of the copper-cadmium residue and cobalt-nickel residue produced by wet zinc smelting purification previously.

Description

Technical field [0001] The invention relates to a wet zinc metallurgy purification method and device, in particular to a wet zinc metallurgy ultrasonic purification method and device under the condition of using ultrasonic waves to improve the activity of zinc powder, and belongs to the technical field of purification. Background technique [0002] In zinc hydrometallurgy, since the zinc sulfate solution produced by leaching zinc ore powder contains copper, cadmium, cobalt, nickel and other impurities, it is necessary to treat the zinc sulfate solution for leaching zinc ore powder. At present, zinc powder is generally used as a reducing agent to remove various impurities in zinc sulfate solution, which is a general purification process in the zinc hydrometallurgy process. However, the current general-purpose purification process consumes high zinc powder, accounting for 3-5% of the output of electrolytic zinc. Moreover, energy consumption has increased substantially, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B19/32
Inventor 曾兴民盛晓敏杨征强娟茹胡原游力挥
Owner XINGMIN TECH ZHUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com