Liquid abrasive and preparation method thereof

A technology of liquid grinding and white corundum powder, which is applied in the aviation field, can solve the problems of not meeting the technical requirements of stainless steel parts for aero-engines, high surface roughness of stainless steel, damage to CNC grinding machines, etc., and achieves good application prospects, short processing time, Equipment damage small effect

Inactive Publication Date: 2009-05-06
SHENYANG LIMING AERO PARTS MFG
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the grinding treatment of domestic stainless steel usually adopts solid abrasive paste or mixed abrasive paste. The surface roughness of stainless steel treated by this type of abrasive is relatively high, which cannot meet the technical requirements of stainless steel parts for aero-engines.
Domestically produced stainless steel abrasives are used in a large amount when processing parts, and the cost performance is not high. At the same time, some abrasives will cause damage to the CNC grinding machine due to composition problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add stearic acid to white corundum powder, mix well; then add beeswax, mix well; then add oleic acid, mix well; then add oleic acid, mix well; then add aviation gasoline, mix well; then add aviation kerosene, mix well Evenly; the mixing ratio is 19% by weight of white corundum, 4.5% of stearic acid, 0.5% of beeswax, 18% of oleic acid, 52% of aviation gasoline, and 6% of aviation kerosene.

[0019] Then it was placed at room temperature for 150 hours to obtain a mixed material.

[0020] The mixed material is kept at 200±5° C. for 10 hours, and then cooled to room temperature to prepare a liquid abrasive.

[0021] Use this liquid abrasive to process the end face sealing surface of the stainless steel sealing seat. The roughness of the processed sealing end face is Ra δ ≤ Ra0.2, and the flatness is 0.0012. Using 1000 ml of this liquid abrasive can process 20 such workpieces, each The processing time of a workpiece is 10 minutes.

[0022] Ordinary abrasive paste is used t...

Embodiment 2

[0024] Add stearic acid to white corundum powder, mix well, then add beeswax, mix well, then add oleic acid, mix well, then add oleic acid, mix well, then add aviation gasoline, mix well, then add aviation kerosene, mix Uniform; the mixing ratio is 20% by weight of white corundum, 3% of stearic acid, 1% of beeswax, 20% of oleic acid, 54% of aviation gasoline, and 2% of aviation kerosene.

[0025] Then it was placed at room temperature for 150 hours to obtain a mixed material.

[0026] The mixed material was kept at 200±5° C. for 11 hours, and then cooled to room temperature to prepare a liquid abrasive.

Embodiment 3

[0028] Add stearic acid to white corundum powder, mix well, then add beeswax, mix well, then add oleic acid, mix well, then add oleic acid, mix well, then add aviation gasoline, mix well, then add aviation kerosene, mix Uniform; mixing ratio by weight percentage is that white corundum accounts for 21%, stearic acid accounts for 3%, beeswax accounts for 1%, oleic acid accounts for 20%, aviation gasoline accounts for 57%, and aviation kerosene accounts for 6%.

[0029] Then keep the temperature at 40° C. for 20 h; obtain the mixed material.

[0030] The mixed material is kept at 200±5° C. for 12 hours, and then cooled to room temperature to prepare a liquid abrasive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides liquid abradant and a preparation method thereof, which belongs to the technical field of materials. The components in weight percentage of the liquid abradant are: 19 to 21 percent of white alundum powder, 3 to 5 percent of stearic acid, 0.5 to 1.5 percent of beeswax, 10 to 20 percent of oleic acid, 52 to 57 percent of aviation gasoline and 2 to 6 percent of aviation kerosene. The preparation method comprises the following steps of mixing the white alundum powder, the stearic acid, the beeswax, the oleic acid, the aviation gasoline and the aviation kerosene so as to obtain a mixed material; preserving the heat of the mixed material for 10 to 12 hours at a temperature of 200+-5 DEG C, cooling the mixed material to room temperature and preparing the mixed material into the liquid abradant. The liquid abradant with the same volume has the advantages of large processing quantity and short processing time. The liquid abradant prepared by the invention is convenient to use and little in harm to equipment, and has good application prospects.

Description

technical field [0001] The invention belongs to the field of aviation technology, in particular to a liquid abrasive and a preparation method thereof. Background technique [0002] At present, the grinding treatment of domestic stainless steel usually adopts solid abrasive paste or mixed state abrasive paste. The surface roughness of stainless steel treated by this type of abrasive is relatively high, which cannot meet the technical requirements of stainless steel parts for aero-engines. Domestically produced stainless steel abrasives are used in a large amount when processing parts, and the cost performance is not high. At the same time, some abrasives will cause damage to the CNC grinding machine due to composition problems. [0003] Therefore, the development of a liquid abrasive that can grind stainless steel to a lower surface roughness has become an urgent problem to be solved. Contents of the invention [0004] In view of the above technical problems, the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K3/14
Inventor 卜锋裴宇飞彭新王博刘明铭黄晨华
Owner SHENYANG LIMING AERO PARTS MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap