High-alumina fine fire clay

A refractory mud, high-alumina technology, applied in the field of refractory materials, can solve the problems of poor fluidity and easy shrinkage of refractory mud, and achieve the effects of extended service life, good ductility, and reduced manufacturing costs.

Inactive Publication Date: 2009-05-13
甄国民 +1
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a high-alumina fine refractory clay in order to solve the problem of poor fluidity and easy shrinkage after calcination of the fireclay used in the industrial kiln existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] Embodiment 1, a high-alumina fine refractory mud is composed of the following raw materials in the weight ratio, high-alumina bauxite clinker powder 46%, sodium carboxymethyl cellulose 5%, purified water 49%. Among them, the specification of high alumina bauxite clinker powder is 0.088mm super high alumina bauxite clinker powder.

[0008] Take the raw materials according to the proportion, and then use a mixer to mix them evenly.

Embodiment 2

[0009] Embodiment 2. A high-alumina fine refractory mud is composed of the following raw materials in the weight ratio, high-alumina bauxite clinker powder 52%, sodium carboxymethyl cellulose 3%, and the rest is 45% of purified water.

[0010] The specification used for high alumina bauxite clinker powder is 0.088mm first-grade high alumina bauxite clinker powder.

[0011] Take the raw materials according to the proportion, then mix and stir evenly.

Embodiment 3

[0012] Embodiment 3, a high-alumina fine refractory mud is composed of the following raw materials in the weight ratio, high-alumina bauxite clinker powder 50%, sodium carboxymethyl cellulose 4%, and the rest is 46% of purified water.

[0013] The specification used for high alumina bauxite clinker powder is 0.088mm Class A high alumina bauxite clinker powder.

[0014] Take the raw materials according to the proportion, then mix and stir evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a refractory material, in particular to high-alumina fine fireclay, which solves the problems that fireclay used by a kiln in the laying industry in the prior art has poor fluidity and is easy to shrink after calcination. The high-alumina fine fireclay consists of the following raw materials in weight percentage: 46 to 52 percent of bauxite chamotte powder, 3 to 5 percent of sodium carboxymethyl cellulose, and the balance being water. The kiln laid by using the high-alumina fine fireclay basically can not be shrunk due to the fireclay, and is subjected to zero deformation basically, so that the service life of the kiln is exponentially prolonged and the production cost of the product is reduced.

Description

technical field [0001] The invention relates to a refractory material, in particular to a high-alumina fine refractory mud. Background technique [0002] The manufacturing method of industrial calcining kilns is generally to build layers of refractory bricks. In order to ensure the tightness of the kiln, refractory bricks with smooth surfaces must be selected, and then bonded with fireclay layer by layer. Refractory bricks become a whole. The refractory brick layer varies according to the number of kiln floors. The fire clay currently used as a binder is generally composed of high-alumina clinker powder, high-alumina raw meal powder, clay powder, and water. Although this kind of fire clay can also play the role of bonding and sealing, many problems have been found in actual use. First, the adhesive contains a large amount of free water, and the adhesive will be burnt by the refractory brick after contacting it. Pore ​​absorption of bricks leads to poor fluidity and poor du...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 甄国民
Owner 甄国民
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com