An anti-rust paint, marine technology, applied in the field of anti-rust paint, can solve the problems of poor adhesion of anti-rust paint, short service life, detachment, etc., to improve adhesion, reduce the number of construction passes, and solve the effects of thixotropy
Inactive Publication Date: 2009-05-13
赵建飞
View PDF0 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The existing anti-rust paint has poor adhesion to steel materials, short service life, often cracks or detachment, and has problems such as thixotropy
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0020] An antirust paint for ships is prepared by mixing and grinding the following raw materials in parts by weight:
[0021] 5-8 parts of epoxy resin (example 5, 7, 8 parts)
[0022] 4-8 parts of butanol (example 4, 6, 8 parts)
example 2
[0023] 2 to 3 parts of phosphoric acid (Example 2, 3 parts)
[0024] 7 to 9 parts of antirust agent (example 7, 8, 9 parts)
[0025] Thickener 6~7 parts (Example 6, 7 parts)
[0026] Dispersant 40~50 parts (Example 40, 45, 50 parts)
[0027] Film-forming agent 7-10 parts (example 7, 9, 10 parts)
[0028] 10-15 parts of basic lead silicate chromate (example 10, 12, 15 parts)
[0029] Coal tar pitch 0~10 parts (Example 1, 5, 10 parts)
[0030] V45 asphalt antirust paint thixotropic agent 2 to 5 parts (example 2, 3, 5 parts)
[0031] 8 to 12 parts of water (example 8, 10, 12 parts).
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses antirust paint for ships, which is prepared by epoxy resin, butanol, phosphoric acid, antirust agent, thickening agent, dispersant, film forming agent, basic lead chromate silicate, coal tar pitch, V45 asphalt antirust paint thixotropic agent and water. The antirust paint has the advantages that the antirust paint not only can effectively solve the thixotropic problem of the paint, but also can improve adhesive force of the paint to a steel material greatly, reduce construction processes, and ensure film thickness of the paint, and has stable physical property of the paint film, low toxicity, chemical medium resistance, and strong weather resistance.
Description
Technical field: [0001] The invention relates to an antirust paint. Background technique: [0002] The existing antirust paint has poor adhesion to steel materials, short service life, often cracks or detachment, and has problems such as thixotropy. Invention content: [0003] The object of the present invention is to provide an antirust paint for ships which has high adhesion to iron and steel materials and can effectively solve the problem of thixotropy. [0004] Technical solution of the present invention is: [0005] An antirust paint for ships is characterized in that: it is made of the following raw materials in parts by weight: [0006] 5-8 parts of epoxy resin [0007] 4-8 parts of butanol [0008] Phosphoric acid 2~3 parts [0009] Antirust agent 7~9 parts [0010] Thickener 6~7 parts [0011] Dispersant 40~50 parts [0012] Film-forming agent 7-10 parts [0013] 10-15 parts of basic lead silicate chromate [0014] Coal tar pitch 0~10 parts [0015] V45...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more