Wood-like co-extrusion PMMA modified material and preparation method thereof

A modified material and imitation wood grain technology, which is applied in the field of imitation wood grain co-extrusion PMMA modified material and its preparation, can solve the problems of insufficient weather resistance, etc., and achieve the effect of strong three-dimensional effect, saving forest resources, and good layering

Inactive Publication Date: 2013-03-27
DONGGUAN JINFULIANG PLASTIC & RUBBER TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] One of the purposes of the present invention is to provide a new imitation wood grain co-extruded PMMA modified material for many defects such as insufficient weather resistance of existing plastic wood grain profiles;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: a kind of imitation mahogany co-extruded PMMA modified material provided by the present embodiment comprises two parts: PMMA base color material and PMMA pattern material, and its weight ratio is: PMMA base color material 80%, PMMA grain material 20% %, specifically, the PMMA base color material and the PMMA texture material respectively include the following components in parts by weight:

[0035] PMMA primer formula: carbon black 0.05%; iron oxide pigment 2%; ultraviolet absorber 0.5%; PMMA 97.45%;

[0036] PMMA texture formula: carbon black 2%; UV absorber 0.5%; PMMA 20%; PET 77.5%.

[0037] The preparation method of above-mentioned imitation mahogany co-extrusion PMMA modified material, it specifically comprises the following steps:

[0038] 1. Preparation of PMMA base color material:

[0039] (1) Weighing: take carbon black, iron oxide pigment, ultraviolet absorber and PMMA according to the formula;

[0040] (2) Mixing: Put the above-mentioned weig...

Embodiment 2

[0051] Embodiment 2: A kind of imitation teak wood co-extruded PMMA modified material and material preparation method thereof provided in this embodiment, its basic components and steps are identical with embodiment 1, and its difference is that its component comprises two parts: The weight ratio of the PMMA base color material and the PMMA texture material is: 90% of the PMMA base color material and 10% of the PMMA texture material. Specifically, wherein the PMMA base color material and the PMMA texture material respectively include the following components in parts by weight: the PMMA base color material formula is: carbon black 0.03%, iron oxide red 1%, iron oxide yellow 1%, ultraviolet absorber 0.5% % and PMMA 97.47%; PMMA texture formula is: carbon black 1%, UV absorber 0.5%, PMMA 20% and PET 78.5%.

[0052] The teak-like co-extruded PMMA / PVC profile can be prepared on a profile co-extrusion production line by using the above-mentioned teak-like co-extruded PMMA modified ...

Embodiment 3

[0053] Embodiment 3: A kind of imitation pine wood co-extruded PMMA modified material and material preparation method thereof provided in this embodiment, its basic components and steps are the same as in Embodiment 1, and its difference is that it comprises two parts: PMMA bottom Colorant and PMMA grain material, its weight ratio is: PMMA base color material 50%, PMMA grain material 50%, concrete, described PMMA base color material and PMMA grain material respectively comprise the component of following weight ratio: wherein PMMA Base color material formula: carbon black 0.01%, iron oxide yellow 3%, ultraviolet absorber 0.5% and PMMA 96.49%; PMMA pattern material formula: carbon black 0.2%, iron oxide yellow 20%, ultraviolet absorber 0.5%, PMMA 20% and PET 59.3%.

[0054] Using the above-mentioned pine-like co-extrusion PMMA modified material, the pine-like co-extrusion PMMA / PVC profiles can be prepared on the profile co-extrusion production line.

[0055] The finished produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a wood-like co-extrusion PMMA modified material, the components of which mainly comprise PMMA ground color material and PMMA grain material, and the weight percentage of the PMMA ground color material and the PMMA grain material is that 50-90 percent of the PMMA ground color material, and 10-50 percent of the PMMA mark material. Plastic steel doors and windows made from the wood-like co-extrusion PMMA modified material has strong viewing and vivid wood grain; can realize the replacement of wood by plastic, thus saving precious wood resources; and has excellent weather resistance, thus widening the application and development of wood-like profiles and being capable of being applied to the manufacturing of indoor and outdoor doors and windows, guardrails, decorative boards, foundation lines, furniture, and the like. The invention also provides the preparation method of the wood-like co-extrusion PMMA modified material, which comprises the steps of weighing, mixing, and extruding. The preparation method is simple, and has extensive raw material resources, low product cost, and wide popularization using value.

Description

technical field [0001] The invention belongs to the field of new material chemistry, and in particular relates to a wood-grain-like co-extruded PMMA modified material and a preparation method thereof. Background technique [0002] In the prior art, home decoration is still based on timber and aluminum alloy profiles. However, wood is expensive, more susceptible to corrosion and decay, which brings inconvenience to life, and excessive use will cause excessive felling of trees, causing damage to the environment. [0003] The production cost of aluminum alloy profiles is high. The production of one ton of aluminum alloy profiles requires 18,650 degrees of electricity from ore to finished products, while the comprehensive power consumption of one ton of plastic profiles is 7,800 degrees from ore to finished products using the calcium carbide method. It can be seen that aluminum The comprehensive power consumption in the manufacturing process of alloy profiles is more than 2.5 t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/12C08K3/04C08K3/22C08K5/132B29B9/00B29C47/92C08L67/02B29C48/92
CPCB29C48/04
Inventor 翟景波陈卫军
Owner DONGGUAN JINFULIANG PLASTIC & RUBBER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap