Dress lining cloth with hot melt adhesive transferred towards fabric after press adhesion

A technology of hot-melt adhesives and fabrics, applied in clothing, clothing, applications, etc., can solve the problems of low peeling strength, poor additive performance, and poor washing resistance, and achieve improved washing resistance, better peeling strength, and prevent seepage. glue effect

Inactive Publication Date: 2009-08-05
江苏三泰轻工科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Hot-melt adhesive is required for hot-melt bonding of interlining and fabric. At present, polyamide or polyester is used as hot-melt adhesive. After pressing and bonding, it will not transfer to the fabric. Smaller, and easy to bleed, at the same time, poor washing resistance
Moreover, the additives currently used are also poor in performance, resulting in low overall washing and dry cleaning resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Water: 65.5%, Dispersant: 1.5%, Lubrication Stabilizer: 3.5%, Cylinder Cleaner: 3%, Defoamer: 0.2%, Polyamide: 10%, Polyester: 5%, High Density Polyethylene: 10%, Thickener: 1.3%. The dispersant is ATESYNTH 61 from Baume (Hangzhou) Chemical Auxiliary Co., Ltd., which is a concentrated solution containing thickening and dispersing components, and can adjust the viscosity when preparing the slurry. The lubricating stabilizer is MIRAPLAST LSF 24 from Baume (Hangzhou) Chemical Auxiliary Co., Ltd., which is suitable for the lubricant of water-based slurry, has pseudoplastic elasticity and viscoelasticity, and internal lubrication. Rotary screen cleaner adopts MIRAPLAST SCR 47 from Baume (Hangzhou) Chemical Auxiliary Co., Ltd., which is a processing aid based on polyacrylate for rotary screen transfer, and is used to prevent adhesion on the roller and dry knot. The defoamer uses TEBEFOM HTS from Baume (Hangzhou) Chemical Auxiliary Co., Ltd., which can withstand high tempera...

Embodiment 2

[0051] Water: 67%, Dispersant: 1%, Lubrication Stabilizer: 3.8%, Cylinder Cleaner: 2.5%, Defoamer: 0.3%, Polyamide: 9%, Polyester: 4%, High Density Polyethylene: 11%, Thickener: 1.4%.

Embodiment 3

[0053] Water: 64%, Dispersant: 1%, Lubrication Stabilizer: 4%, Cylinder Cleaner: 3.3%, Defoamer: 0.1%, Polyamide: 11%, Polyester: 6%, High Density Polyethylene: 9.4%, Thickener: 1.2%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses clothes padding cloth capable of transferring hot melt adhesive to fabric after pressing and adhering, which comprises base cloth and a paste point coating. The paste point coating comprises the following components in percentage by weight: 64 to 67 percent of water, 1 to 2 percent of dispersant, 3 to 4 percent of lubricating and stabilizing agent, 2.5 to 3.5 percent of circular screen cleaning agent, 0.1 to 0.3 percent of antifoaming agent, 9 to 11 percent of polyamide, 4 to 6 percent of polyester, 9 to 11 percent of high density polyethylene, and 1.2 to 1.4 percent of thickening agent. The high density polyethylene of which the melting point is higher than those of the polyamide and the polyester is added into the paste point component, and the adhering and pressing temperature is between the two melting point temperatures of the polyamide and the polyester, so that the high density polyethylene is semi-melted, can be partially transferred to the fabric; the special component is adopted for transferring 50 percent of the whole hot melt adhesive to the fabric, and the other 50 percent of the hot melt adhesive is reserved on the padding cloth, so the clothes padding cloth reaches the optimal peeling strength, can also prevent adhesive seepage, and improve water washing resistance definitely; and by adopting assistants such as the dispersant, the lubricating and stabilizing agent, the antifoaming agent, the thickening agent, and the like, the water washing resistance and the dry cleaning resistance of the product are optimal.

Description

【Technical field】 [0001] The invention relates to a clothing interlining, in particular to a clothing interlining which can transfer hot melt adhesive to fabrics after pressing and bonding. 【Background technique】 [0002] my country is a big country in clothing, and the current annual output of clothing is about 20 billion pieces. With the improvement of people's requirements for clothing, most clothing currently uses interlining, and 80%-90% of clothing in my country also uses fusible interlining. [0003] Hot-melt adhesive is required for hot-melt bonding of interlining and fabric. At present, polyamide or polyester is used as hot-melt adhesive. After pressing and bonding, it will not transfer to the fabric. It is small and easy to bleed. At the same time, it has poor washing resistance. Moreover, the additives currently used are also poor in performance, resulting in low overall washing and dry cleaning resistance. 【Content of invention】 [0004] The object of the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A41D27/02
Inventor 段国平钱晓明余永生左志忠
Owner 江苏三泰轻工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap