Antistatic urethane elastic fiber production technology

A production process and antistatic technology, applied in the manufacture of conductive/antistatic filaments, textiles and papermaking, single-component synthetic polymer rayon, etc. The effect of improving spinning performance, improving rheology and increasing polymer molecular weight

Inactive Publication Date: 2009-09-09
连云港杜钟氨纶有限公司
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antistatic agent will cause the instability of the spinning oil, and a higher oiling rate is required to ensure the antistatic effect, and an excessively high oiling rate makes it easy to "rewind" during the unwinding process of spandex yarn The phenomenon of broken wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Example 1. An antistatic spandex production process includes adding an antistatic agent to the spinning stock solution for producing spandex, and the added amount of the antistatic agent is 1% of the solid content in the spinning stock solution.

Embodiment 2

[0020] Example 2. An antistatic spandex production process includes adding an antistatic agent to the spinning stock solution for producing spandex, and the added amount of the antistatic agent is 2% of the solid content in the spinning stock solution.

Embodiment 3

[0021] Example 3. An antistatic spandex production process includes adding an antistatic agent to the spinning stock solution for producing spandex, and the added amount of the antistatic agent is 3% of the solid content in the spinning stock solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an antistatic polyurethane production technology which is characterized in that spinning dope for producing urethane elastic fire is added with antistatic agent; the addition amount of the antistatic agent is 1 to 5 percent of the solid content in the spinning dope; and the antistatic agent is anionic antistatic agent, cationic antistatic agent, ampholytic type antistatic agent or non-ionic antistatic agent. The antistatic performance of the antistatic polyurethane filament prepared by the technology has significant advantages to the conventional polyurethane filament under the condition of using same spinning finish; under the conditions with the temperature of 25 DEG C and the relative humidity of 65 percent, the half life of the antistatic polyurethane filament is near 0s, the static voltage is less than 1kV, and the specific resistance is less than 108 omega*cm; and the invention is suitable for back-end purposes such as high-speed tricot warping, cotton bale, and the like.

Description

technical field [0001] The invention relates to a spandex production process, in particular to an antistatic spandex production process. Background technique [0002] Due to the poor antistatic effect of spandex fibers, in order to prevent the fibers from attracting each other due to static electricity in the subsequent use process, as well as attracting short fibers to fly and causing problems such as broken filaments and uneven tension, the traditional production process needs to be added to the spinning oil. A certain proportion of antistatic agent. However, the antistatic agent will cause the instability of the spinning oil, and a higher oiling rate is required to ensure the antistatic effect, and an excessively high oiling rate makes it easy to "rewind" during the unwinding process of spandex yarn The phenomenon of broken wires. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an antistatic spandex producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/94D01F1/09
Inventor 胡爱林汪宝华张斌孙振波张星明孙迎春
Owner 连云港杜钟氨纶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com