Nanometer porcelain shellac varnish and preparation method thereof

A production method and nanotechnology, applied in the direction of coating, can solve the problems of polluted atmospheric environment, poor protection, large latex particles, etc., and achieve the effects of promoting metabolism, strong adhesion, and strong water and crack resistance.

Active Publication Date: 2013-04-03
杨宝根 +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Both coatings have their own shortcomings: the former contains a large amount of organic volatiles, which will volatilize into the atmosphere no matter during the production or use of the coatings, polluting the atmospheric environment
It has caused great harm to people, especially the industrial workers in this industry and the paint users in the construction industry; and the latter, although the emission of organic volatiles has been reduced and air pollution has been reduced, but due to its large latex particles and poor compactness, its Poor water resistance, poor protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A kind of nano porcelain glue paint, its composition is: Shuangfei powder 50.4%, ash calcium powder 33.6%, cellulose ether 16%. Described double flying powder is: heavy calcium carbonate; Ash calcium powder is: Ca(OH) 2, CaO and a small amount of CaCO 3 mixture;

[0012] Prepare Shuangfei powder, ash calcium powder, and cellulose ether according to the weight ratio: 50.4:33.6:16, mix evenly, pour into a tamping machine, and fully stir for 30-60 minutes. It can be made into powdered nano-enamel paint.

Embodiment 2

[0014] A kind of nano porcelain glue paint, its composition is: Shuangfei powder 50.4%, ash calcium powder 33.6%, cellulose ether 16%. Described double flying powder is: heavy calcium carbonate; Ash calcium powder is: Ca(OH) 2, CaO and a small amount of CaCO 3 mixture;

[0015] Prepare Shuangfei powder, ash calcium powder, and cellulose ether according to the weight ratio: 50.4:33.6:16, then add 14.5% pure water, and stir with a mixer at high speed until it matures into a jelly. It can be made into colloidal nano-enamel paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a nanometer porcelain shellac varnish and a preparation method thereof; the shellac varnish has the components as follows: 50.4 percent of calcium carbonate, 33.6 percent of ash-calcium-powder, and 16 percent of cellulose ether. The preparation method comprises the following steps: the calcium carbonate, the ash-calcium-powder and the cellulose ether are prepared at the weight ratio of 50.4:33.6:16 and are evenly mixed, poured into a masher and fully stirred. Compared with the prior art, the invention has the advantages that the nanometer porcelain shellac varnish hasthe permanent electrode, can discompose the water molecule in the air under normal temperature, produces a plurality of negative ions of air without ozone and plays the role of health care to human body as the nanometer porcelain shellac varnish adopts the advanced nanometer dispersion technology and is compounded by the natural mountain meal associated with a modifying agent. The nanometer porcelain shellac varnish can discompose and absorb the carbon monoxide, hydronitrogen and other poisonous and harmful substances in the air by photocatalysis, purify the air and promote the human metabolism. In addition, the nanometer porcelain shellac varnish has the advantages of good air permeability, strong adhesive power, high hardness and strong water resistance and crack resistance.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a nano-enamel paint and a preparation method thereof. Background technique [0002] At present, most of the coatings circulating on the market are organic solvent-based coatings and water-soluble coatings. Both coatings have their own shortcomings: the former contains a large amount of organic volatiles, which will volatilize into the atmosphere no matter during the production or use of the coatings, polluting the atmospheric environment. It has caused great harm to people, especially the industrial workers in this industry and the paint users in the construction industry; and the latter, although the emission of organic volatiles has been reduced and air pollution has been reduced, but due to its large latex particles and poor compactness, its Poor water resistance means poor protection. Contents of the invention [0003] The technical problem to be solved by the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine