Producing technique of films for aluminized anti-fake wrapping paper
A production process and technology for wrapping paper, which is applied in the field of production process of films used for aluminized anti-counterfeiting wrapping paper, can solve the problems of poor transferability, temperature difference, poor reusability of polyester film, etc., so as to improve transfer performance and economy effect of benefit
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example one:
[0018] A production process of a laser transfer film used for cigarette packaging anti-counterfeiting paper. The production process includes the following steps:
[0019] (1) Load the polyester film and molded paint on the coating machine. The five-section oven of the coating machine is set to 85°C, 110°C, 140°C, 125°C, and 100°C, and a 150-line electro-engraved wire roller is used for coating, so that the coating dry amount is controlled at 1.0-1.4 g / m². The coating speed is generally controlled at 80-100 m / min, and the coating viscosity of the coating is controlled for 25-40 seconds (Zahn 3# cup); when the coating viscosity is too high, use ethyl acetate or n-propyl acetate Dilute the paint.
[0020] (2) Put the coated polyester film on the moulding machine. The moulding machine is equipped with a nickel plate with a holographic pattern required by a cigarette, and the coated surface of the polyester film is in contact with the nickel plate with a holograph...
Example Embodiment
[0025] Embodiment two:
[0026] A production process of a laser transfer film for a certain toothpaste packaging anti-counterfeiting paper. The production process includes the following steps
[0027] (1) Load the polyester film and molded paint on the coating machine. The five-section oven of the coating machine is set to 75°C, 120°C, 135°C, 115°C, and 90°C, and a 165-line electro-engraved wire roller is used for coating, so that the coating dry amount is controlled at 1.1 to 1.5 g / m². The coating speed is generally controlled at 90-110 m / min, and the coating viscosity of the coating is controlled for 28-45 seconds (Zahn 3# cup); when the coating viscosity of the coating is too high, use ethyl acetate or n-propyl acetate Dilute the paint.
[0028] (2) Put the coated polyester film on the moulding machine. The moulding machine is equipped with a nickel plate with a holographic pattern required by a cigarette, and the coated surface of the polyester film is in contact with the nick...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap