Polymer electric heating heat carrier and preparation method thereof

A technology of electric heating and heat carrier, applied in the field of electric heaters, can solve the problems of high power consumption, flammability, toxicity, etc., and achieve the effect of low power consumption and good environmental performance

Inactive Publication Date: 2010-10-06
蔡万龙
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a polymer electric heating heat carrier and a preparation method thereof, which can solve the problems of flammability, toxicity, and large power consumption in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Prepare 1000g of polymer electric heating heat carrier, 1) Add 200g of deionized water into a stainless steel tank and heat it to about 75°C;

[0030] 2) Add 50g of edible baking powder;

[0031] 3) Add 50g of neotame;

[0032] 4) Add 20g of edible fruit green;

[0033] 5) Add 30g of edible D-isoVC sodium;

[0034] 6) Add 200g of edible molecularly distilled glyceride, stir to dissolve, boil for 5 minutes, and cool completely for later use;

[0035] 7) When using, add 150g of edible ethanol with a concentration of 50%, 100g of edible glycerin, and 200g of edible peanut oil, and stir to dissolve.

[0036] Experimental verification: After using the above-mentioned polymer electric heating heat carrier, the electric heater is continuously turned on for 48 hours in the zero temperature zone of the cold storage at 0°C, the temperature is 98-105°C, and the power of the electric heating tube is 1000W, which is higher than the existing electric heating The minimum power of ...

Embodiment 2

[0038] Prepare 1000g of polymer electric heating heat carrier, 1) Add 200g of deionized water into a stainless steel tank and heat it to about 70°C;

[0039] 2) Add 40g of edible baking powder;

[0040] 3) Add 20g of neotame;

[0041] 4) Add 40g of edible D-isoVC sodium;

[0042] 5) Add 250g of edible molecularly distilled glyceride, stir to dissolve, boil for 5 minutes, and cool completely for later use;

[0043] 6) When using, add 150g of edible ethanol with a concentration of 50%, 50g of edible glycerin, and 250g of edible peanut oil, and stir to dissolve.

[0044] Experimental verification: After using the above-mentioned polymer electric heating heat carrier, the electric heater is continuously turned on for 48 hours in the zero temperature zone of the cold storage at 0°C, the temperature is 95-98°C, and the power of the electric heating tube is 1000W, which is higher than that of the existing electric heater. The minimum power of the heater is more than 2000W, which i...

Embodiment 3

[0046] Prepare 1000g of polymer electric heating heat carrier, 1) Add 300g of deionized water into a stainless steel tank and heat it to about 75°C;

[0047] 2) Add 50g of edible baking powder;

[0048] 3) Add 50g of neotame;

[0049] 4) Add edible sodium D-isoVC 50g;

[0050] 5) Add 300g of edible molecularly distilled glyceride, stir to dissolve, boil for 5 minutes, and cool completely for later use;

[0051] 6) When using, add 100g of edible ethanol with a concentration of 50%, 50g of edible glycerin, and 100g of edible soybean oil, and stir to dissolve.

[0052] Experimental verification: After using the above-mentioned polymer electric heating heat carrier, the electric heater is continuously turned on for 48 hours in the zero temperature range of the cold storage at 0°C, the temperature is 85-90°C, and the power of the electric heating tube is 800W, which is higher than that of the existing electric heater. The minimum power of the heater is more than 2000W, which is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polymer electric heating heat carrier and a preparation method thereof and can solve the flammable, toxic and high-electric consumption problems of the prior art. The invention adopts a technical proposal that: the polymer electric heating heat carrier comprises the following components by weight percentage: 20 to 30 percent of deionized water, 5 to 10 percent of edible propanetriol, 10 to 20 percent of edible ethanol, 4 to 5 percent of edible baking powder, 2 to 5 percent of edible neotame, 3 to 5 percent of edible D-sodium isovitamin C, 20 to 30 percent of thicker and 10 to 25 percent of edible oil. Electric heaters using the polymer electric heating heat carrier has the advantages of energy conservation, environmental protection, low production cost and high temperature.

Description

technical field [0001] The invention belongs to the technical field of electric heaters, and in particular relates to a polymer electric heating heat carrier used in electric heaters and a preparation method thereof. Background technique [0002] At present, the annual production of oil-filled electric heaters in Ningbo, Zhejiang Province is 30 million units, and the annual export is 22 million units. % biphenyl and 73.5% mixture of diphenyl ether). The guide oil has a high boiling point (258°C) (370°C can be used for 750-1100 days); it is flammable but has no explosion hazard; its toxicity is very slight; its main disadvantage is that it is easy to penetrate soft asbestos fillers, and all pipe flanges Metal gaskets are required at the connection. [0003] The heating method used by the electric oil well electric heater is mineral oil heating. High temperature No. 45 engine oil and high temperature No. 60 engine oil are commonly used in production, and the heating tempera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K5/04
CPCY02P20/10
Inventor 蔡万龙
Owner 蔡万龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com