Method for preparing boracic low-alloy high-speed steel rolls

A low-alloy, high-speed steel technology, applied in the field of roll manufacturing, can solve the problems of high production costs and achieve the effects of short cycle, safe use, and low energy consumption for heat treatment

Inactive Publication Date: 2011-01-05
BEIJING UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned roll material has excellent wear resistance, but contains more alloying elements, so the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing boracic low-alloy high-speed steel rolls
  • Method for preparing boracic low-alloy high-speed steel rolls
  • Method for preparing boracic low-alloy high-speed steel rolls

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

Embodiment 2

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing boracic low-alloy high-speed steel rolls, which is characterized by comprising the following steps: firstly carrying out metal mold casting of the roll, wherein a roll body is made of boracic low-alloy high-speed steel, and a roll core is made of ductile cast iron; putting the roll into a heating furnace at the temperature of lower than 200 DEG C after rough machining, preserving heat for 1-3 hours, then heating to the temperature of 520-580 DEG C at the temperature rising speed of 15-25 DEG C per hour, and air cooling after heat preservation; and then, putting the roll into the heating furnace at the temperature of lower than 300 DEG C again, preserving heat for 1-2 hours, then heating to the temperature of 480-510 DEG C at the temperature rising speed of 28-40 DEG C per hour, cooling the furnace to the temperature of lower than 180 DEG C after heat preservation, and air cooling to the room temperature. The method not only has low energy consumption and a short heating processing period, but also has good use effect when being used for the heating processing of the boracic low-alloy high-speed steel roll.

Description

Method for preparing boron-containing low-alloy high-speed steel roll Technical field The invention belongs to the technical field of roll manufacturing, and specifically relates to a method for preparing a roll, in particular to a method for preparing a boron-containing low-alloy high-speed steel roll. Background technique Rolls are the main consumable parts in the production of steel rolling. The research on improving the wear resistance of rolls has always attracted attention at home and abroad. The use of high-speed steel instead of high-chromium cast iron, nickel-chromium cast iron, chromium-molybdenum cast iron and nickel-chromium-molybdenum cast iron to manufacture rolls is the main way to improve the wear resistance of rolls. Japanese Patent Publication JP6330235 discloses the chemical composition of a centrifugal cast high-speed steel roll material as follows: C: 1.4-2.6%, Si: 0.2-1.5%, Mn<1.5%, Cr: 3-8%, (2Mo+W) : 6-14%, V: 4-8%, Ti: 0.3-2.5%, the balance Fe. Un...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D19/16C21D9/38
Inventor 符寒光雷永平戴建方邢建东
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products