Duplex stainless steel with pitting corrosion resistance and favourable cold temperature flexibility and manufacturing method thereof

A technology of duplex stainless steel and low temperature toughness, which is applied in the field of duplex stainless steel and its manufacturing to achieve excellent pitting corrosion resistance, reduce adverse effects and improve corrosion resistance.

Inactive Publication Date: 2010-03-31
BAOSHAN IRON & STEEL CO LTD
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of manganese on the corrosion resistance of stainless steel is basically negative

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Duplex stainless steel with pitting corrosion resistance and favourable cold temperature flexibility and manufacturing method thereof
  • Duplex stainless steel with pitting corrosion resistance and favourable cold temperature flexibility and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The alloy metallographic diagram of embodiment 1 is as figure 1 Shown (austenite phase accounts for about 50%), the rule that the impact value of the alloy of embodiment 2 changes with temperature is as follows figure 2 shown. Table 2 shows the mechanical properties and corrosion properties of the steels of the present invention and comparative steels, as well as the results of edge cracks during hot working. Among them, the phase ratio of duplex stainless steel adopts quantitative metallographic method, and the sample is electrolytically corroded, and the corrosion agent is 40g KOH+100ml H 2 O, corrosion current 0.3~0.8A / cm 2 ;The mechanical properties are taken from the hot-rolled annealed plate, and the impact properties are in accordance with the GB / T229 Charpy V-notch impact standard, the sample size is 10×10×55mm, and the test temperatures are 20°C, 0°C, -20°C, - 40°C, -60°C. The anti-pitting corrosion equivalent is calculated according to the general formula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a duplex stainless steel with pitting corrosion resistance and favourable cold temperature flexibility and a manufacturing method thereof. The duplex stainless steel comprisesthe following components in mass percentage: 0.01-0.10% of C, 0.2-1.0% of Si, more than 0% and less than 1.5% of Mn, 20.0-22.0% of Cr, 1.8-4.0% of Ni, 0.08-0.2% of N, more than 0% and less than 0.5% of Mo, less than or equal to 1.0% of one or more than one of W and Cu and the balance Fe and inevitable impurities. The invention controls Mn content below 1.5% until zero and simultaneously adjusts the content of elements of N, Ni and the like to ensure that steel has high strength, favourable corrosion resistance and favourable impact toughness at room temperature and low temperature when steel contains no or small amount of noble element Mo; meanwhile, the duplex stainless steel has low cost and small hot working difficulty, can be largely applied in the fields of buildings along the coast,petrochemical industry and the like and can replace 304 austenitic stainless steel of which the nickel content is above 8% at room temperature and lower temperature.

Description

Technical field [0001] The present invention relates to duplex stainless steel and its manufacturing method, in particular to a duplex stainless steel with excellent pitting corrosion resistance and low temperature toughness and its manufacturing method. Background technique [0002] Duplex stainless steel is composed of two phases of ferrite and austenite, and the proportion of each phase is not less than 30%. Due to the characteristics of the two-phase structure, duplex stainless steel has the advantages of both ferritic stainless steel and austenitic stainless steel. Compared with ferritic stainless steel, it has high toughness, low brittle transition temperature, intergranular corrosion resistance and good welding performance. At the same time, the advantages of ferritic steel with high thermal conductivity and small expansion coefficient are retained. Its yield strength is significantly higher than that of austenitic stainless steel, its chloride stress corrosion crack...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/44C21D8/02C21D1/26
Inventor 张伟胡锦程宋红梅江来珠王治宇崔健
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com