Low-cost steel plate for building structure and manufacturing method thereof

A low-cost technology for building structures, applied in the manufacture of converters, furnace types, furnaces, etc., can solve the problems of high production process cost, high alloy cost, high P content, and achieve laminar tear resistance and good, strong and toughness. Good, low-cost results

Inactive Publication Date: 2010-05-12
SHOUGANG CORPORATION
View PDF4 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The steel is added with V alloy elements, and the cost is high; the content of S and P is high, and the maximum thickness of the steel plate is only 60mm
[0004] The Chinese invention patent with the patent number 01133562.9 discloses a high-performance fire-resistant and weather-resistant construction steel and its production method. The steel contains Mo, Ni, Cr, Cu, Ti, Nb, V and other alloying elements, and the alloy cost is high ; The steel adopts normalizing + tempering process after rolling, and the production process cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The actual composition of the steel plate of the present invention (percentage by weight): C 0.15%, Si 0.38%, Mn 1.36%, P 0.010%, S 0.003%, Alt 0.036%, carbon equivalent Ceq is 0.38%, and the balance is Fe and unavoidable sandwich. Rolled into a steel plate with a thickness of 80mm, the properties of the steel plate: yield strength 370Mpa, tensile strength 525Mpa, yield ratio 0.70, elongation 30.5%, -40°C longitudinal impact energy (AKV) 119J, 94J, 132J, Z-direction reduction of area 55.0 %, 52.0%, 59.5%.

[0034] Production method of the present invention is as follows:

[0035](1) Hot metal pretreatment: hot metal S 0.035% before desulfurization, Si≤0.42%, and hot metal S after desulfurization 0.004%.

[0036] (2) Smelting process: The molten iron is smelted in a converter, and 300kg of Al iron / furnace is added when the steel is tapped, and then sent to the LF refining furnace for desulfurization and deoxidation treatment, and then RH vacuum treatment, the vacuum ti...

Embodiment 2

[0042] The actual composition (percentage by weight) of the steel plate of the present invention: C 0.17%, Si0.36%, Mn 1.40%, P 0.009%, S 0.002%, Alt 0.042%, carbon equivalent Ceq is 0.41%, and the balance is Fe and Inevitable interstitial. Rolled into a thick 36mm steel plate, its steel plate properties: yield strength 415Mpa, tensile strength 545Mpa, yield strength ratio 0.76, elongation 29.0%, -40 ℃ longitudinal impact energy (AKV) is 125J, 104J, 144J, Z-direction reduction of area 61.0%, 57.0%, and 60.5%.

[0043] Production method of the present invention is as follows:

[0044] (1) Hot metal pretreatment: hot metal S 0.035% before desulfurization, Si≤0.44%, and hot metal S after desulfurization 0.0046%.

[0045] (2) Smelting process: Smelt the molten iron in a converter, add 290kg of Al iron / furnace when tapping the steel, then send it to the LF refining furnace for desulfurization and deoxidation treatment, and then perform RH vacuum treatment, the vacuum time is 14 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-cost steel plate for a building structure and a manufacturing method thereof. The steel plate comprises the following chemical components: C accounts for 0.14 percent to 0.17 percent, Si accounts for 0.20 percent to 0.50 percent, Mn accounts for 1.30 percent to 1.50 percent, P is equal to or less than 0.012 percent, S is equal to or less than 0.005 percent, Alt accounts for 0.020 percent to 0.060 percent, and the balances are Fe and unavoidable foreign impurities. (1) No noble metal elements such as Nb, V, Ti, Ni, Cr, Mo and the like, are added in the steel, the requirement of Q345GJ strength level is met completely though the chemical components C-Si-Mn-Al, and the cost is low; (2) the steel is purer, P is equal to or less than 0.012 percent, and S is equal to or less than 0.005 percent; (3) the impact toughness is good at the temperature of minus 40 DEG C, and the Charpy impact energy of a V-shaped notch is equal to or higher than 80 J; (4) the earthquake resistance is good, and the actual yield ratio is respectively smaller than 0.78; and (5) the lamellar tearing resistance is excellent, and the actual Z-direction section shrinkage ratio in the total-thickness direction is equal to or higher than 38 percent. The hot-rolling Q345GJEZ35 steel plate used for the building structure and provided with thickness of 20-90 mm can be produced, and the steel plate and the manufacturing method can be applied to the manufacture of the steel structure of the high-rise building, have good comprehensive performance and simple production process, can realize the batch production and have low cost.

Description

technical field [0001] The invention relates to a steel plate for low-cost building structure, which is applied to the steel structure of high-rise buildings, and also relates to a production method of the steel plate for low-cost building structure. Background technique [0002] At present, steel for building structures has been used in the domestic construction field, but the steel products with the same strength level or greater than that of the present invention are all based on the basic chemical composition of C-Si-Mn-Al, and Nb, V, Ti, Ni, One or more of Cr, Mo and other elements. [0003] The Chinese invention patent with the patent number 200810104298.5 discloses a steel plate for high-rise buildings. The steel is characterized in that the chemical composition is C: 0.12-0.17%, Si: 0.30-0.45%, and Mn: 1.35-1.55%. , P: ≤0.022%, S: ≤0.010%, Alt: 0.020-0.050%, V: 0.03-0.10%. The steel is added with V alloy elements, and the cost is high; the content of S and P is hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/06C21C7/064C21C5/28C21C7/06C21C7/10C21D9/52B21B37/74B21B37/16
Inventor 李春智王根矶姜中行郑会平刘春明何元春顾林豪沈开照王全礼白学军郝宁刘印良
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products