Thermoplastic elastomer composition for bonding ABS and preparation method thereof

A technology of thermoplastic elastomers and compositions, applied in the field of thermoplastic elastomers, can solve the problems of high price and weak bonding, and achieve good bonding and broad application prospects

Inactive Publication Date: 2010-06-30
SHANGHAI SUNNY
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the TPE modified materials that can be used to bond ABS and PC on the market mainly have the disadvantages of weak bonding and high prices. The bonding materials prepared by this method not only have high bonding strength, but also are relatively cheap, and have great market potential

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～2

[0031] Proportioning (weight %) sees table 1.

[0032] Table 1

[0033] raw material name

[0034] Put all the components into SEBS and naphthenic oil in a high mixer and mix for 3-5 minutes, then add other raw materials and mix for 3-5 minutes, the processing temperature is 180, 185, 195, 200, 200, 200, 200, 200, 190°C, screw rotation at 300 rpm.

[0035] For the thermoplastic elastomer composition used for bonding ABS obtained in the examples, the mechanical properties were tested by ASTM. See Table 2 for the sample performance comparison table of Example 1 and Example 2.

[0036] Table 2

[0037] Test items

[0038] Test items

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a thermoplastic elastomer composition for bonding ABS and a preparation method thereof. The composition is prepared by raw materials with the following weight proportion: 40 to 70 percents of polyurethane (TPU), 5 to 20 percents of SEBS, 10 to 30 percents of extending oil, 2 to 5 percents of SEBS-g-MAH, 0 to 30 percents of active calcium carbonate and 0.1 to 0.5 percent of antioxidant. The preparation method comprises the following steps of: weighting the raw materials according to weight proportion, mixing SEBS and white oil evenly in high mixing machine, then adding other raw materials and mixing for 2 to 5 minutes, discharging; putting the raw materials mixed evenly into an extruser for prilling. The invention has the characters that the prepared thermoplastic elastomer not only has good bonding property with ABS and PC, but also has adjustable hardness according to the client requirements, and can be used for producing handle sheath, cushion pad, and the like.

Description

technical field [0001] The invention relates to a thermoplastic elastomer composition for bonding ABS and a preparation method thereof. The material has excellent bonding performance with ABS and PC, can be directly injected, and belongs to the technical field of thermoplastic elastomers. Background technique [0002] With the continuous improvement of people's product requirements, the demand for TPE modified materials that can be used to bond ABS and PC continues to increase. This kind of TPE is mainly used in the fields of handle coating materials and sheath materials. At present, the TPE modified materials that can be used to bond ABS and PC on the market mainly have the disadvantages of weak adhesion and high price. The adhesive prepared by this method not only has high bonding strength, but also is relatively cheap, and has Great market potential. Contents of the invention [0003] The purpose of the present invention is to provide a thermoplastic elastomer composit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/06C08K13/02B29B9/00B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/9259B29C2948/92885
Inventor 孟成铭杨涛项军陈晓东
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com