Longquan celadon reinforced blank and preparation method of product thereof

The technology of celadon and blank is applied in the field of preparation of Longquan celadon reinforced blank and its products, which can solve the problems of low strength of Longquan celadon, and achieve the effects of increasing sales profit, increasing comprehensive cost and remarkable economic benefit.

Inactive Publication Date: 2012-08-22
ZHEJIANG UNIV
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In order to solve the problem of low strength of Longquan celadon, the invention provides a preparation method of Longquan celadon reinforced blank and its products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Longquan celadon reinforced blank and preparation method of product thereof
  • Longquan celadon reinforced blank and preparation method of product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Pass 82g of Longquan local celadon mud powder through a 200-mesh sieve, mix with 3g of 120-mesh waste porcelain powder and 15g of 40-80nm nano-α-Al 2 o 3 The powder is mixed and stirred evenly, and the slurry is turned into a slurry and stale (as a grouting material for standby).

[0036] Then grouting molding, after demoulding and drying, the billet is repaired to replenish water, and after natural drying, it is bisque fired at 700°C for 6 hours. Heat at 1350°C for 1 hour and fire.

[0037] The flexural strength of the obtained product was 79.67mpa.

Embodiment 2

[0039] Pass 77g of Longquan local celadon mud powder through a 200-mesh sieve, mix with 3g of 120-mesh waste porcelain powder and 20g of 40-80nm nano-α-Al 2 o 3 The powder is mixed and stirred evenly, and the slurry is turned into a slurry and stale (as a grouting material for standby).

[0040] Then grouting molding, after demoulding and drying, the billet is repaired to replenish water, and after natural drying, it is biscuit fired at 800 ° C for 6 hours. After the bisque fired body is dipped in glaze and dried, it is fired in a high-temperature liquefied gas kiln with a maximum temperature of 1360 ° C. ℃ for 1 hour and fired.

[0041] The flexural strength of the obtained product was 88.25mpa.

Embodiment 3

[0043] Pass 70g of Longquan local celadon mud powder through a 200-mesh sieve, mix with 2g of 120-mesh waste porcelain powder and 25g of 40-80nm nano-α-Al 2 o 3 The powder is mixed and stirred evenly, and the slurry is turned into a slurry and stale (as a grouting material for standby).

[0044] Then grouting molding, after demoulding and drying, the billet is repaired to replenish water, and after natural drying, it is bisque fired at 800°C for 6 hours. After the bisque fired billet is dipped in glaze and dried, it is then fired in a high-temperature liquefied gas kiln with a maximum temperature of 1380 °C. ℃ for 1 hour and fired.

[0045] The flexural strength of the obtained product was 103.06mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Longquan celadon reinforced blank. The Longquan celadon reinforced blank comprises the following components in percentage by weight: 12-25% of alpha-Al2O3 powder, 71-87% of celadon paste powder, and 1-4% of waste porcelain powder. The invention also discloses a method for preparing a product by sintering the Longquan celadon reinforced blank. Under the premise of not changing the characteristics of the traditional Longquan celadon formula, process technology, product style and the like, the invention prepares the Longquan celadon blank with high strength by utilizingalpha-Al2O3 new materials; and since the process technical route is fundamentally not changed, and the sintering and loading device and the sintering system are not changed, the damage rate of the products is greatly reduced due to the high strength of the products and the economical benefit is remarkable.

Description

technical field [0001] The invention relates to a Longquan celadon reinforced blank and a preparation method thereof, belonging to the production fields of Longquan celadon daily-use porcelain, architectural decorative porcelain, and packaging porcelain (wine bottles). Background technique [0002] Longquan celadon rose in the late Tang and Five Dynasties, reached its peak from the Southern Song Dynasty to the Yuan Dynasty, and began to decline after the late Ming Dynasty. The production history lasted for thousands of years. It is a kiln with the longest firing time, the widest distribution and the greatest influence in the history of Chinese porcelain making. Tie. Longquan kiln produces a wide variety and high quality, especially famous for its "thousand peaks emerald color" and "ice-like jade" crystal glaze. For a long time, Longquan celadon has brought convenience and beauty to people's daily life. Over the long years, Longquan celadon, as the carrier of Chinese culture...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/00C04B35/622
Inventor 周少华金逸林彭勃
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com