Anticorrosive nanometer aqueous architectural coating and preparation method thereof

A water-based paint, nano-pigment technology, applied in anti-corrosion paint, coating and other directions, to achieve the effect of strong corrosion resistance, smooth coating, easy to use

Active Publication Date: 2012-03-21
INNER MONGOLIA XINGTAI CONSTRAL GRP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, water-based anti-corrosion coatings made of modified nano-pigments (especially modified nano-zirconia) have not been reported at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] 1. Preparation of modified nano-zirconia

[0013] And the modified nano zirconium dioxide is prepared by the following method: Weigh 10g of zirconium carbonate, add excess sulfuric acid and stir to obtain zirconium sulfate; prepare 1N ammonium bicarbonate solution, add dropwise to zirconium sulfate at a speed of 10-15ml / min solution; keep stirring until the precipitation is complete, after standing still, filter with suction, wash, then extract with absolute ethanol, dry the obtained solid, then burn at a high temperature above 350°C, cool and grind, after measurement, more than 90% The particle size of the particles is less than 100nm to obtain nano zirconium dioxide; put 10g of the above-prepared nano zirconium dioxide in 300mL of absolute ethanol, stir and reflux for 30min, stop the reflux, keep the temperature at 70°C, add stearic acid, and continue stirring 1h, cooling, filtering and drying to obtain modified nano zirconia.

[0014] 2. Preparation of Coatings

[...

Embodiment 2

[0017] 1. Preparation of modified nano-zirconia

[0018] Preparation method is the same as above embodiment 1

[0019] 2. Preparation of Coatings

[0020] Take each raw material according to the following weight ratio: modified nano-zirconia 55, water 30, water-soluble acrylic resin 40, commercially available P-1001, commercially available PS-6302, polyurethane 5, commercially available Sell ​​DH-1700

[0021] 3. Hydroxypropyl methylcellulose 1, commercially available DH-3040.5, commercially available SPG-100.2, titanate 5, AMP-950.15; modified nano-zirconia, water-soluble acrylic resin, P-100, DH -304 and stir evenly, then add water, PS-630, polyurethane, DH-1700, hydroxypropyl methylcellulose, SPG-10 and titanate, stir again, and then emulsify for 30 minutes using a high-speed shear emulsifier , and finally add AMP-95 and stir evenly.

Embodiment 3

[0023] 1. Preparation of modified nano-zirconia

[0024] Preparation method is the same as above embodiment 1

[0025] 2. Preparation of Coatings

[0026] Take each raw material according to the following weight ratio: modified nano-zirconia 35, water 10, water-soluble acrylic resin 25, commercially available P-1000.05, commercially available PS-6300.5, polyurethane 3, commercially available Selling DH-17002, hydroxypropyl methylcellulose 0.5, commercially available DH-3040.1, commercially available SPG-100.01, titanate 3, AMP-950.05; modified nano zirconium dioxide, water-soluble acrylic resin, P- 100. Stir DH-304 evenly, then add water, PS-630, polyurethane, DH-1700, hydroxypropyl methylcellulose, SPG-10 and titanate, stir evenly again, and then use a high-speed shear emulsifier, Emulsify for 30 minutes, finally add AMP-95 and stir evenly.

[0027] The anti-corrosion nano water-based paint of the present invention has the following advantages: all water-soluble components...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an anticorrosive nanometer aqueous architectural coating which is prepared by using modified nano-scale pigment (particularly modified nano-zirconia) as a basis and then mixing with other nonpoisonous materials, has good anticorrosive effect, particularly resists ultraviolet rays, does not contain solvents, is nonpoisonous and environment-friendly and is particularly applicable for the anticorrosion of metals, particularly, outdoor metal components.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof. Specifically, the present invention relates to a nanometer water-based architectural coating for preventing metal corrosion and a preparation method thereof. Background technique [0002] Metal corrosion has brought huge losses to the national economy. In my country, the economic loss caused by metal corrosion is as high as 30 billion yuan, accounting for 4% of the gross national product. Various techniques have been used to protect metals from corrosion for a long time. One of the most effective and commonly used methods for metal equipment is to coat the metal surface with a protective coating to isolate the contact between the corrosive medium and the metal substrate. At present, the anti-corrosion coatings coated on metal surfaces are usually solvent-based coatings. Although they have an effect of inhibiting corrosion, they pose an environmental pollution problem because they ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D7/12C09D5/08
Inventor 王喆苏仲杰韩平王静波致栓明李飞云郝林高亮王晓梅张永军解成刚尚振国马政
Owner INNER MONGOLIA XINGTAI CONSTRAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap