Polyester-aramid guide bearing, thrust disc friction pair and manufacturing method thereof

A manufacturing method and thrust plate technology, applied in the direction of rotating bearings, bearings, bearing components, etc., to achieve the effects of bearing large axial force, improving wear resistance, and good acid and alkali resistance

Active Publication Date: 2011-06-08
沈阳深潜泵业有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a friction pair composed of polyester or aramid guide bearing and thrust plate friction plate and its manufacturing method, its purpose is to solve the current Due to the common problems of poor wear resistance, easy to break, cumbersome process, and environmental pollution in the guide bearings and thrust plate friction plates of submersible motors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester-aramid guide bearing, thrust disc friction pair and manufacturing method thereof
  • Polyester-aramid guide bearing, thrust disc friction pair and manufacturing method thereof
  • Polyester-aramid guide bearing, thrust disc friction pair and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A polyester or aramid guide bearing and a thrust plate friction plate, characterized in that: the guide bearing 1 and the thrust plate friction plate 3 made of polyester or aramid form a pair of friction pairs; the outside of the guide bearing 1 is a pipe wall 15. There is also a water flow groove 16 in the pipe wall 15; the thrust plate friction plate 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction plate 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 is 0.5mm, and the warp and weft density is 48 pieces / 10cm; the thickness of the thrust plate friction plate 3 is 0.5mm.

[0044] A method for manufacturing polyester, aramid guide bearings and thrust disc friction plates as described above, characterized in that:

[0045] The method consists of the following steps:

[0046] (1) Manufacture of the guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for 2 hour...

Embodiment 2

[0053] A polyester or aramid guide bearing and a thrust plate friction plate, characterized in that: the guide bearing 1 and the thrust plate friction plate 3 made of polyester or aramid form a pair of friction pairs; the outside of the guide bearing 1 is a pipe wall 15. There is also a water flow groove 16 in the pipe wall 15; the thrust plate friction plate 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction plate 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 is 0.8mm, and the warp and weft density is 90 pieces / 10cm; the thickness of the friction plate 3 of the thrust plate is 0.8mm.

[0054] A method for manufacturing polyester, aramid guide bearings and thrust disc friction plates as described above, characterized in that:

[0055] The method consists of the following steps:

[0056] (1) Manufacture of the guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for...

Embodiment 3

[0063] A polyester or aramid guide bearing and a thrust plate friction plate, characterized in that: the guide bearing 1 and the thrust plate friction plate 3 made of polyester or aramid form a pair of friction pairs; the outside of the guide bearing 1 is a pipe wall 15. There is also a water flow groove 16 in the pipe wall 15; the thrust plate friction plate 3 and the cast iron base 4 constitute the thrust plate 2, and the thrust plate friction plate 3 is arranged on the cast iron base 4; the thickness of the guide bearing 1 is 0.6mm, and the warp and weft density is 60 pieces / 10cm; the thickness of the friction plate 3 of the thrust plate is 0.6mm.

[0064] A method for manufacturing polyester, aramid guide bearings and thrust disc friction plates as described above, characterized in that:

[0065] The method consists of the following steps:

[0066] (1) Manufacture of the guide bearing: impregnate polyester or aramid cloth with polyvinyl butyral modified phenolic resin for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyester-aramid guide bearing, a thrust disc friction plate and a manufacturing method thereof. The invention is characterized in that the guide bearing made of polyester and aramid and the thrust disc friction plate form a friction pair; the outer part of the guide bearing is a tube wall, and a water flow groove is arranged in the tube wall; and the thrust disc frictionplate is arranged on a cast iron base. The manufacturing method comprises the following steps: drying polyester-aramid resin cloth soaked with polyvinyl butyral modified phenolic resin, extruding thecloth with a tube coiling machine, placing the cloth into a guide bearing compression die and a thrust disc friction plate formation die, and pressing for formation under the certain pressure and certain temperature. The invention improves the wear resistance and mechanical strength of the polyester-aramid guide bearing and the thrust disc friction plate manufactured in the method. Moreover, the polyester-aramid guide bearing and the thrust disc friction plate have the advantages of simple structure, low cost, less pollution, long service life and the like.

Description

1. Technical field: [0001] The invention belongs to the technical field of lubricating bearing manufacturing, and mainly relates to a friction pair composed of a guide bearing made of polyester or aramid and a friction plate of a thrust plate and a manufacturing method thereof, in particular to a friction pair for a submersible motor. A friction pair composed of a guide bearing made of polyester or aramid and a friction plate of a thrust plate and a manufacturing method thereof. 2. Background technology: [0002] In the past, the domestically produced guide bearings for submersible motors were generally made of ZQpb25-5 lead bronze through casting and machining. The disadvantage is that a large amount of lead elements overflow and pollute the environment during the casting process, which is very harmful to people; This kind of bearing requires a large gap between the shaft and the guide bearing, generally 0.19mm, so it is easy to cause uneven air gap between the rotor and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F16C17/08F16C33/20
Inventor 李思泉
Owner 沈阳深潜泵业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More