Powder ash air-entrained concrete building block and preparation method thereof

A technology of air-entrained concrete and fly ash, which is used in the manufacture of tools, ceramic products, climate sustainability, etc., can solve the problems of poor sound insulation effect and heavy block weight, achieve good thermal insulation performance, improve masonry speed, The effect of saving heating and cooling energy

Inactive Publication Date: 2010-12-15
舟山市宇锦新型墙体材料有限公司
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But it also has the above disadvantages: that is, the weight of the block is relatively large and the sound insulation effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] According to the preparation method of the above-mentioned formula, the fly ash aerated concrete block comprises the following steps successively:

[0029] a. Raw material preparation: First, mix the dry materials of cement and lime with each other and stir evenly, then mix the fly ash with water and stir for 3 hours to form a slurry, and control the temperature of the slurry within the range of 43°C, then put the aluminum Add powder and foam stabilizer to the slurry and stir for 0.5 minutes, then mix the slurry with aluminum powder and foam stabilizer and the dry mixture of cement and lime mixed together to form a mixed slurry, and Control the slurry to stir evenly at a temperature of 43°C until the fluidity of the slurry is controlled at 22-25cm;

[0030] b. Pour the slurry with a fluidity of 22 to 25 cm into the mold body. Before the slurry is poured into the mold body, apply a release agent on the side of the mold body, and place the mold with the slurry The body w...

Embodiment 4

[0050] Embodiment four: the basic composition of the formula of the fly ash aerated concrete block of the present embodiment is as follows:

[0051] It is prepared by adding 100kg of cement, 350kg of lime, 1350kg of fly ash, 120kg of waste slurry, 1.4kg of aluminum powder, 0.195kg of foam stabilizer and adding water; the waste slurry is a slurry made of fly ash, lime, cement and water. A foam mixture, or a paste mixture formed by mixing two phases of water, cement, fly ash and lime; the foam stabilizer is: rosin or bone glue. The slurry mixture of 35-50kg of fly ash, 10-30kg of lime, 10-15kg of cement and water in the above waste slurry, or water and 10-15kg of cement, 35-50kg of fly ash, and 10-30kg of lime A slurry mixture formed by mixing the two phases.

[0052] According to the preparation method of the above-mentioned formula, the fly ash aerated concrete block comprises the following steps successively:

[0053] a. Preparation of raw materials: First, mix and stir the...

Embodiment 5

[0058] Embodiment five: the basic composition of the formula of the fly ash aerated concrete block of the present embodiment is as follows:

[0059] It is prepared by adding 150kg of cement, 360kg of lime, 1450kg of fly ash, 125kg of waste slurry, 1.45kg of aluminum powder, 0.2kg of foam stabilizer and adding water; 35~50kg of fly ash, 10~30kg of lime, and 10~ A slurry mixture of 15kg mixed with water, or a slurry mixture of water mixed with 10-15kg of cement, 35-50kg of fly ash, and 10-30kg of lime. The foam stabilizer is: rosin or bone glue.

[0060] According to the preparation method of the above-mentioned formula, the fly ash aerated concrete block comprises the following steps successively:

[0061] a. Raw material preparation: First, mix and stir the dry materials of cement and lime evenly, then mix the waste slurry, fly ash and water and stir for 3.5 hours to form a slurry; and control the temperature of the slurry within the range of 44°C , then add aluminum powder ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a powder ash air-entrained concrete building block and a preparation method thereof. The powder ash air-entrained concrete building block is prepared by adding water to 100-200kg of cement, 350-380kg of lime, 1350-1550kg of powder ash, 1.4-1.5kg of aluminite powder and 0.195-0.205kg of foam stabilizers. The preparation method comprises the following steps of raw material preparation, metering, stirring, pouring in a mould, standing for procuring, demoulding, swinging to cutting parts for cutting, steaming and curing in a reactor and finished product warehousing. The building block has the advantages of light weight, good heat insulation, machinability, convenient construction, wide source of raw materials, high production efficiency, low production energy consumption and good fire protection and sound insulation, wherein the dry volume density of the building block is 500-700kg / m3 and amounts to one third of a clay brick; as a large quantity of air holes and micro holes are arranged inside the building block, the building block has favorable heat insulation; as coarse aggregates are not used, the building block has favorable machinability, can be sawn, dug,drilled and nailed and bonded by bonding materials, thereby providing beneficial conditions for building construction; and the building block belongs to a green environmental-protection product.

Description

technical field [0001] The invention relates to the technical field of making an autoclaved aerated concrete block, in particular to an autoclaved fly ash aerated concrete block and a preparation method thereof. Background technique [0002] There is an existing Chinese invention patent whose application number is CN200910304521.5 and the title is "A Kind of Phosphorous Slag Autoclaved Aerated Concrete Block and Its Preparation Method", which discloses an autoclaved aerated concrete block and its preparation method, which is It is prepared by adding water to phosphorus slag, silica sand, quicklime, cement, gypsum and aluminum powder. Compared with the prior art, this invention uses the waste slag produced by the production of phosphorus as the main material to provide siliceous components to produce autoclaved aerated concrete blocks, heat preservation, and can produce different levels of autoclaved aerated concrete blocks according to different requirements . While making...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/10B28B1/14
CPCC04B2111/28C04B40/0032C04B28/18C04B2111/52C04B2103/48Y02W30/91
Inventor 王全省
Owner 舟山市宇锦新型墙体材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.