Preparation method of marine coating emulsion

A paint and emulsion technology, applied in the field of ship paint emulsion preparation, can solve the problems of asphalt carcinogenicity, poor anti-corrosion effect, long-term anti-corrosion, short curing time, etc., so as to achieve the effect of no environmental pollution and elimination of construction hazards.

Inactive Publication Date: 2011-02-02
NANTONG REPAIR AIR CHEM BIOENG
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the lack of one-component chlorinated rubber aluminum powder thick coating primer and asphalt anti-corrosion aluminum powder primer due to poor anti-corrosion effect and the suspicion of carcinogenicity of asphalt, the anti-corrosion coating now requires low surface treatment adaptability, environmental protection, long-term anti-corrosion, and curing time. to be short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1: Preparation method of marine paint emulsion, the steps and parameters of the method are:

[0013] (1) Dissolve 1631 surfactant and OP emulsifier with 50℃-55℃ hot water in a ratio of 3:7, and cool;

[0014] (2) Put the neoprene latex into the mixing tank, gradually add the 1631 surfactant and water solution while stirring, add in the ratio 5:5, and the stirring time is 5-10 minutes;

[0015] (3) Put the OP emulsified solution and the water solution into the chlorine partial emulsion, add it in a ratio of 3:7, and stir for 3 to 5 minutes;

[0016] (4) Put the chloroprene mixed emulsion into the chloroprene mixed emulsion and stir, according to the ratio of 4:6, gradually add while stirring, stir for 10 minutes and add the defoamer at the same time.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a marine coating emulsion, which comprise the following steps of: (1) respectively dissolving a 1631 surfactant and an OP (Polyoxyethylene Pctylphenol Ether) emulsifier with 50-55 DEG C of hot water according to the ratio of 3:7, and cooling; (2) pouring neoprene latex in an agitating tank, and agitating for 5-10 min while gradually adding the 1631 surfactant and the water solution according to the ratio of 5:5; (3) pouring the OP emulsification solution and the water solution into a chlorine partial emulsion according to the ratio of 3:7, and stirring for 3-5 min; and (4) pouring the chlorine partial emulsion into the neoprene mixture emulsion according to the ratio of 4:6, and stirring for 10 min while gradually pouring a defoamer. Because the hot water is used as an additive and no solvent is used, the preparation method has the advantages of environmental protection and no environmental pollution, and the construction harm of the traditional coating is eliminated.

Description

1. Technical Field [0001] The invention relates to a method for preparing a marine paint emulsion. 2. Background technology [0002] Anti-corrosion coating is to coat corrosion-resistant coating on the metal surface, after curing into a film, it has the functions of shielding, corrosion resistance and electrochemistry. Coating anti-corrosion coatings on metal surfaces is the most economical, effective, and most commonly used method of metal anti-corrosion. The anti-corrosion coating used on the metal of marine environment ships must have good adhesion and a certain mechanical strength. The cured coating can firmly adhere to the metal substrate and have a certain mechanical strength to ensure that it can withstand work The role of various forces under the conditions should also have the following special properties. (1) Salt spray resistance. Due to the strong electrolyte environment formed by sea water or salt spray in the ocean, the metal in this environment is easily ionized...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D111/02C09D5/16C09D5/08
Inventor 葛兴元
Owner NANTONG REPAIR AIR CHEM BIOENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com