Printed label tape and manufacturing method thereof

A production method and technology of trademark tapes, which are applied to dry-cleaning fiber products, textiles, fabrics, etc., can solve the problems of trademark fading, poor production technology, and containing harmful substances to the human body, and achieve low production costs and improved solubility.

Active Publication Date: 2011-06-08
HUZHOU SINY LABEL MATERIAL
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the production efficiency of printed trademarks is high and accepted by most manufacturers, it has strict technical requirements. If the production technology is not strong, it is easy to cause the trademarks to fade, to make the fabrics using the trademarks stained with variegated colors, and to use them The fabric of the trademark fades and the trademark has a variety of technical problems such as high formaldehyde content, high pH value, and harmful substances to the human body.
The most serious problem is that when the existing printed trademark is applied to dark-colored textile products, it is easy to react with dark-colored dyes, causing the dark color of textile products to become lighter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Printed label tape and manufacturing method thereof
  • Printed label tape and manufacturing method thereof
  • Printed label tape and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A printed trademark tape, which includes a gray cloth layer 1 and a glue layer 2, the thickness of which is 125 μm, and the thickness of the gray cloth layer is 120 μm; its residual chloride ion content is less than or equal to 1.28%.

[0040] The manufacturing method of the above-mentioned printed trademark tape is as follows:

[0041] ①Choose waste nylon yarn, then pick out the non-nylon components, and then mix magnesium chloride and magnesium sulfate to dissolve in toluene to make glue for dipping the grey cloth. The specific component distribution ratio of the glue is as follows:

[0042] Nylon 10wt%

[0043] Magnesium sulfate 10wt%

[0044] Magnesium chloride 10wt%

[0045] Toluene 70wt%

[0046] ②After the nylon grey cloth is cleaned, immerse it in the above glue to apply glue to the grey cloth. The amount of glue applied is controlled to 25g / m 2 ;

[0047] ③The coated cloth obtained by gluing treatment is cleaned in dechlorinated water at a temperature of 20~30℃, and the was...

Embodiment 2

[0050] A printed trademark tape, which includes a gray cloth layer 1 and a glue layer 2, the thickness of which is 130 μm, and the thickness of the gray cloth layer is 125 μm; its residual chloride ion content is ≤1.34%.

[0051] The manufacturing method of the above-mentioned printed trademark tape is as follows:

[0052] ①Choose waste nylon yarn, then pick out the non-nylon components, and then mix calcium chloride and calcium sulfate to dissolve in butyl acrylate to make a glue for dipping the grey cloth. The specific composition of the glue is such as under,

[0053] Nylon 12wt%

[0054] Calcium sulfate 12wt%

[0055] Calcium chloride 12wt%

[0056] Butyl acrylate 64wt%

[0057] ②After the nylon grey cloth is cleaned, immerse it in the above glue to apply glue to the grey cloth. The amount of glue applied is controlled to 28g / m 2 ;

[0058] ③The coated cloth obtained by gluing treatment is cleaned in dechlorinated water at a temperature of 20~30℃, and the washing time is 5~10min; the ...

Embodiment 3

[0061] A printed trademark belt, which includes a gray cloth layer 1 and a glue layer 2, its thickness is 135 μm, and the thickness of the gray cloth layer is 130 μm; its residual chloride ion content is less than or equal to 1.39%.

[0062] The manufacturing method of the above-mentioned printed trademark tape is as follows:

[0063] ①Choose waste nylon yarn, then pick out the non-nylon components in it, then mix magnesium chloride and calcium carbonate to dissolve in methanol to make glue for dipping the grey cloth. The specific component distribution ratio of the glue is as follows:

[0064] Nylon 13wt%

[0065] Calcium carbonate 13wt%

[0066] Magnesium chloride 13wt%

[0067] Methanol 61wt%

[0068] ②After the nylon grey cloth is cleaned, immerse it in the above glue to apply glue to the grey cloth. The amount of glue is controlled to 30g / m 2 ;

[0069] ③The coated cloth obtained by gluing treatment is cleaned in dechlorinated water at a temperature of 20~30℃, and the washing time is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a printed label tape and a manufacturing method thereof, belonging to the technical field of printed label manufacturing. The printed label tape comprises a grey fabric layer and an adhesive layer, and the thickness of the printed label tape is 120-150 mu m, wherein the thickness of the grey fabric layer is 120-130 mu m; the pH value of the printed label tape is 7.5-9.0; and the content of the residual chloride ions is less than or equal to 1.51%. The manufacturing method of the printed label tape comprises a coating treatment step and an aftertreatment step, wherein in the coating treatment step, the grey fabric is glued in a dipping manner; and the gluing formula comprises 20-30wt% of accelerant which contains chlorides, and the chloride content does not exceed 50wt% of the accelerant. The printed label tape provided by the invention can not react with textile products, can not discolor the textile products, and has the advantage of low production cost as compared with the label tapes produced by other methods.

Description

Technical field [0001] The invention relates to a printed trademark tape and a manufacturing method thereof, belonging to the technical field of printed trademark manufacturing. Background technique [0002] According to its manufacturing method, trademark belts can be divided into woven trademark belts, printed trademark belts and embroidered trademark belts. Embroidered trademarks are high-grade trademark decorations, which are mostly used in brand-name clothing, high-end clothing, and some special-purpose products. At present, the scope of use is relatively small. Woven trademark belt, also known as silk woven trademark belt, is woven in the form of multiple shuttle boxes, multiple reeds, and multiple specifications on a jacquard loom. It is currently the most widely used trademark in clothing, shoes, hats, and towels. A kind of product logo, it can weave a variety of trademark patterns and text. The raw materials used in woven trademark belts are generally bleached or dyed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/12D03D15/00D06M11/155D06M11/56D06M11/76D06M15/59D06L1/12
Inventor 黄梦礼吴根土潘叶华
Owner HUZHOU SINY LABEL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap