Acrylonitrile butadiene styrene (ABS) resin composition with good flowability

A technology of ABS resin and flow performance, which is applied in the field of ABS resin composition, can solve the problems of complex polymerization modification process, lack of flow performance, large performance loss, etc., and achieve low cost, wide processing range and simple production process Effect

Inactive Publication Date: 2011-06-29
PETROCHINA CO LTD
View PDF0 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the above-mentioned methods, the polymerization modification process is complicated, and large-scale petrochemicals are often required for the production of special varieties during production, and a large amount of transition materials will inevitably be caused when switchin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Preparation of high flow ABS special material

[0010] formula:

[0011] SAN1 30 kg

[0012] SAN2 50 kg

[0013] High rubber content ABS grafting powder 20 kg

[0014] N,N-ethylene bisstearamide 1.1 kg

[0015] Magnesium stearate 0.15 kg

[0016] Distearyl pentaerythritol diphosphite 0.1 kg

[0017] preparation:

[0018] First, mix the raw materials prepared according to the formula in a high-speed mixer at a medium speed for 3 minutes, and then add them into a twin-screw extruder for blending. Then it is cooled by cooling water and granulated to become a cylindrical particle product of Φ3×3mm.

[0019] Process conditions:

[0020] The first stage 190°C, the second stage 200°C, the third stage 200°C, the fourth stage 205°C, the fifth stage 205°C, the sixth stage 208°C, the seventh stage 208°C, the eighth stage 208°C, the ninth stage Section 208°C, die temperature 210°C.

[0021] Screw speed: 200 rpm.

Embodiment 2

[0023] Preparation of high flow ABS special material

[0024] formula:

[0025] SAN1 12 kg

[0026] SAN2 60 kg

[0027] High rubber content ABS grafting powder 28 kg

[0028] N,N-ethylene bisstearamide 1.5 kg

[0029] Magnesium stearate 0.18 kg

[0030] Distearyl pentaerythritol diphosphite 0.15 kg

[0031] preparation:

[0032] First, mix the raw materials prepared according to the formula in a high-speed mixer at a medium speed for 3 minutes, and then add them into a twin-screw extruder for blending. Then it is cooled by cooling water and granulated to become a cylindrical particle product of Φ3×3mm.

[0033] Process conditions:

[0034] The first stage 190°C, the second stage 200°C, the third stage 200°C, the fourth stage 205°C, the fifth stage 205°C, the sixth stage 208°C, the seventh stage 208°C, the eighth stage 208°C, the ninth stage Section 208°C, die temperature 210°C.

[0035] Screw speed: 200 rpm.

Embodiment 3

[0037] Preparation of high flow ABS special material

[0038] formula:

[0039] SAN1 16 kg

[0040] SAN2 60 kg

[0041] High rubber content ABS grafting powder 24 kg

[0042] N,N-ethylene bisstearamide 1.0 kg

[0043] Magnesium stearate 0.15 kg

[0044] Distearyl pentaerythritol diphosphite 0.1 kg

[0045] preparation:

[0046] First, mix the raw materials prepared according to the formula in a high-speed mixer at a medium speed for 3 minutes, and then add them into a twin-screw extruder for blending. Then it is cooled by cooling water and granulated to become a cylindrical particle product of Φ3×3mm.

[0047] Process conditions:

[0048] The first stage 190°C, the second stage 200°C, the third stage 200°C, the fourth stage 205°C, the fifth stage 205°C, the sixth stage 208°C, the seventh stage 208°C, the eighth stage 208°C, the ninth stage Section 208°C, die temperature 210°C.

[0049] Screw speed: 200 rpm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an acrylonitrile butadiene styrene (ABS) resin composition with good flowability. The composition comprises the following components in parts by weight: 20-30 parts of butadiene-styrene-acrylonitrile grafted copolymer with the resin content of above 60%, 10-30 parts of styrene-acrylonitrile copolymer with the acrylonitrile (AN) content of 22.5-24.5 and the number-average molecular weight of 7000-8000, 70-40 parts of styrene-acrylonitrile copolymer with the AN content of 23.5-25.5 and the number-average molecular weight of 4000-5000, 1.0-2.5 parts of N,N-ethylene bis stearamide, 0.1-0.4 part of magnesium stearate and 0.1-0.2 part of dialkypentaerythitoldiphosphite. Processing can be carried out at the temperature of 200-260 DEG C; the melt index of the resin composition is 40-70g/min; and the resin composition has the advantages of good mechanical property, simple production process and relatively low cost.

Description

Technical field: [0001] The invention relates to an ABS resin composition with excellent fluidity at 200°C-260°C and a melt index of 40-70g / min. Background technique: [0002] my country is the world's largest producer and consumer of household appliances. The consumption ratio of ABS resin in household appliances has remained high at about 60%. At the same time, the focus of the ABS resin market is gradually shifting to office equipment, automobiles, transportation and communication and building materials. and other fields. Nowadays, the increasingly detailed requirements for materials make ABS resins used in different application fields have different special properties. With the emergence and popularization of flat-panel TVs and the reduction in the cost of LCD screens, it will bring an explosion to the LCD TV industry. The production of components such as LCD TV backplanes requires the modification of ABS resin, which requires a large number of high-flow ABS resin produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/12C08L55/02C08K5/20C08K5/098C08K5/524
Inventor 王洪梅赵新刚张海霞宋振彪陈兴郁朱海波郝刚宋立忠闫柏郁王玉岩曲茵
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap