Zeolite-like lightweight heat preservation and sound insulation board and production method thereof

A thermal insulation and sound insulation, zeolite-like technology, applied in the direction of cement production, etc., can solve the problems of difficult processing and degradation, white pollution, environmental hazards, etc., to achieve the effect of delaying the setting time, good effect, and strong sound absorption effect

Active Publication Date: 2011-08-31
广骏新材料科技股份有限公司
View PDF3 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In recent years, EPS boards have been used in many fields, but most of them are for one-time use. Therefore, there are about tens of millions of cub

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] 1. Formula and preparation of dry powder slurry

[0020] Fly Ash 79%

[0021] Phosphorus slag 10%

[0022] Compound basic activator 10.7%

[0023] Polypropylene fiber 0.3%

[0024] According to the above weight ratio, each component is stirred evenly to prepare a dry powder slurry, wherein the composite alkali activator is to add analytically pure NaOH solution to the industrial water glass solution with a modulus of 3.2, and adjust its modulus to 1.2. Na 2 O content is 9%;

[0025] 2. Preparation of light heat insulation and sound insulation board

[0026] Take 90 parts of the above-mentioned dry powder slurry and 10 parts of EPS granules, mix them well and press them into a mold for molding, demould after 1 day of molding, and maintain at 60°C for 3 days; the EPS granules are made by crushing waste EPS boards into a particle size of 3mm particles.

[0027] 3. Sheet performance

[0028] Bulk density is 500kg / m 3 , the 28d compressive strength is 7.6Mpa, the th...

Embodiment 2

[0030] 1. Formula and preparation of dry powder slurry

[0031] Fly Ash 79%

[0032] Phosphorus slag 10%

[0033] Compound basic activator 10.7%

[0034] Polyester 0.3%

[0035] According to the above weight ratio, each component is stirred evenly to prepare a dry powder slurry, wherein the composite alkali activator is to add analytically pure NaOH solution to the industrial water glass solution with a modulus of 3.2, and adjust its modulus to 1.2. Na 2 O content is 9%;

[0036] 2. Preparation of light heat insulation and sound insulation board

[0037] Take 92 parts of the above-mentioned dry powder slurry and 8 parts of EPS granules, mix them well and press them into a mold for molding, demould after 1 day of molding, and maintain at 60°C for 4 days; the EPS granules are made by crushing waste EPS boards into a particle size of 2mm particles.

[0038] 3. Sheet performance

[0039] Bulk density is 800kg / m 3 , the 28d compressive strength is 11.8Mpa, the thermal cond...

Embodiment 3

[0041] 1. Formula and preparation of dry powder slurry

[0042] Fly Ash 75%

[0043] Phosphorus slag 15%

[0044] Basic activator 9.7%

[0045] Polyacrylonitrile fiber 0.3%

[0046] According to the above weight ratio, each component is stirred evenly to prepare a dry powder slurry, wherein the composite alkali activator is to add analytically pure NaOH solution to the industrial water glass solution with a modulus of 3.2, and adjust its modulus to 1.2. Na 2 The O content is 9%.

[0047] 2. Preparation of light heat insulation and sound insulation board

[0048] Take 90 parts of the above-mentioned dry powder slurry and 10 parts of EPS granules, mix them well and press them into a mold for molding, demoulding after 1 day of molding, and curing at 60°C for 3 days; the EPS granules are made by crushing waste EPS boards into 4mm particles.

[0049] 3. Sheet performance

[0050] The bulk density is 510kg / m 3, the 28d compressive strength is 7.1Mpa, the thermal conductivit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to view more

Abstract

The invention provides a zeolite-like lightweight heat preservation and sound insulation board applied to a building outer wall, or wall filling of a nonbearing wall or a building top layer. The board comprises dry powder slurry and lightweight aggregate, wherein the dry powder slurry is a zeolite-like geopolymer formed by the excitation of a composite alkali excitant and comprises the following components in percentage by weight: 70-85 percent of coal ash, 5-15 percent of phosphorus slag, 8-20 percent of composite alkali excitant and 0.1-0.3 percent of anticracking fiber; the lightweight aggregate is EPS (Expandable Polystyrene) granules; and the charge ratio of the dry powder slurry to the lightweight aggregate is (89-95): (5-15). The zeolite-like lightweight heat preservation and soundinsulation board has low volume weight, high compression strength, favorable heat preservation and heat insulation properties and good sound absorption effect on various frequency bands of sound waves. The invention also provides a production method of the zeolite-like lightweight heat preservation and sound insulation board. The method has simple process conditions and is easy to realize.

Description

technical field [0001] The invention relates to a thermal insulation and sound insulation board, in particular to a lightweight thermal insulation and sound insulation board applied to building exterior walls or non-load-bearing wall filling or building top floors, and more particularly relates to a geopolymer used as a gelling The material is applied to building exterior walls or non-load-bearing wall fillings or zeolite-type lightweight thermal insulation and sound insulation panels on the top layer of buildings. The invention also relates to a preparation method of the zeolite-type lightweight heat-insulating and sound-insulating board. Background technique [0002] The traditional thermal insulation board is made of polystyrene foam particles, cement, foaming agent and stabilizer after stirring and molding and curing. Cement is a traditional cementitious material. Due to its high resources, high energy consumption, and high carbon emissions, it is less and less in line ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B16/08
CPCC04B28/008Y02P40/10C04B16/08
Inventor 曹青林华强洪永顺张铬
Owner 广骏新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka