Method for manufacturing chemical anti-counterfeiting paper
A production method and technology for anti-counterfeiting paper, which are applied in papermaking, textiles and papermaking, and addition of non-polymeric organic compounds, etc., can solve the problems of inauthentic counterfeit products, difficulty in distinguishing authenticity, and limited first-line anti-counterfeiting effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] This embodiment is for making base paper containing phenolphthalein, and 40% phenolphthalein aqueous solution is taken as an example.
[0015] Weigh 5 kg of phenolphthalein, put it in a container, add 7.5 kg of clear water, stir the phenolphthalein in the water evenly, then move the aqueous solution to a ball mill and grind until the particle size is about 15 μm, take it out, and add it to 820 kg of base paper filler with a solid content of 20.0% ( The proportion of phenolphthalein in the base paper filler is 3%), fully stirred evenly, and the prepared coating is passed through a 100-mesh sieve to be used for making base paper.
[0016] Base paper copying steps are:
[0017] A. Beating. The beating concentration is 3.0%~4.0%, and the beating degree is 34~360SR;
[0018] B. Sizing. Online concentration: 0.4%~0.5%, filler (filler prepared above) addition amount: 30~35l / min, pH value: 4.3~4.8, sizing agent in slurry: 2~4 l / min;
[0019] C. Forming. Vacuum degree of va...
Embodiment 2
[0029] This example is a carbonless copy CF paper coated with phenolphthalein. Take 60% phenolphthalein aqueous solution as an example.
[0030] Weigh 3 kg of phenolphthalein, put it in a container, add 2 kg of clear water, stir the phenolphthalein in the water evenly, then move the aqueous solution to a ball mill and grind it to about 10 μm, take it out, and add it to 1068 kg of carbon-free carbon copying CF paper coating with a solid content of 28.0% (use The proportion of phenolphthalein in the carbonless copying CF paper coating is 1%), stir well, pass the prepared coating through a 120 mesh sieve, and coat the carbonless copying CF paper as usual.
[0031] Paper coating steps are:
[0032] A. Coating. Transport the above prepared coating to the coating machine, coat one side of the paper, adjust the air knife air pressure to control the coating amount at 3~5g / m2;
[0033] B. Drying. The coated paper enters the first stage of drying, and the drying temperature is contr...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com