Non-base-return color ceramic tile joint mixture

A technology of colored ceramic tiles and caulking agent, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of slow curing speed, inconvenient production, transportation and storage, etc. The problem of alkali return, the effect of convenient transportation and storage

Inactive Publication Date: 2011-09-14
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD +2
View PDF3 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this material can completely solve the problem of alkali return, it is inconvenient in production, transportation and storage, the width and depth of the gap filled are limited, and the curing speed is relatively slow.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-base-return color ceramic tile joint mixture
  • Non-base-return color ceramic tile joint mixture

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0035] Based on the above range, the present invention provides the first embodiment, and the specific weight ratio of each component is as follows:

[0036] No. 42.5 white quick-hardening sulfoaluminate cement 450.0;

[0037] 300 mesh ~ 400 mesh heavy calcium 522.0;

[0038] Hydroxypropyl methylcellulose ether 0.5;

[0039] Ethylene, vinyl chloride and vinyl lauricate rubber powder 15.0;

[0040] Lignin fiber 1.5;

[0041] Polypropylene fiber 0.5;

[0042] Thixotropic agent 1.0;

[0043] Superplasticizer 2.0;

[0044] Retarder 4.0;

[0045] Antifungal agent 1.5;

[0046] Hydrophobic agent 2.0;

[0047] Pigment 0.

[0048] Based on the above range, the present invention provides a second embodiment, and the specific weight ratio of each component is as follows:

[0049] No. 42.5 white quick-hardening sulfoaluminate cement 350.0;

[0050] 300 mesh to 400 mesh heavy calcium 579.8;

[0051] Hydroxypropyl methylcellulose ether 1.0;

[0052] Ethylene, vinyl chloride an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a safe environment-friendly non-base-return color ceramic tile joint mixture. The safe environment-friendly non-base-return color ceramic tile joint mixture comprises the following components in percentage by weight: 30 to 50 percent of white cement, 40 to 75 percent of filler, 0.03 to 0.30 percent of cellulose ether, 0.50 to 5 percent of adhesive, 0.05 to 0.40 percent of cellulose fiber, 0 to 0.10 percent of chemical fiber, 0 to 0.40 percent of thixotropic agent, 0 to 0.70 percent of water reducing agent, 0 to 0.80 percent of retarder, 0 to 0.4 percent of mildew preventive, 0 to 0.25 percent of water repellent and 0 to 5 percent of ferric oxide series pigment. The safe environment-friendly non-base-return color ceramic tile joint mixture can solve the base return problem of the joint mixture radically and has the advantages of moderate price, safety, environmental friendliness, convenience of production, transportation and storage, wide usable range and the like.

Description

technical field [0001] The invention relates to a safe, environment-friendly and non-alkali-returning colored tile gap filler used for filling gaps between indoor and outdoor tiles of buildings. Background technique [0002] With the development of society, tiles have become one of the most commonly used materials in architectural decoration. In order to avoid hollowing between tiles due to thermal expansion and contraction, a certain gap needs to be reserved between tiles, and the gap needs to be filled with building materials. Initially, the filling material used was mixed on-site by ordinary white Portland cement and heavy calcium or other white fillers in a certain proportion. Due to the shortcomings of the filling material randomly mixed on site, such as high rigidity, insufficient hydration, large water absorption and monotonous color, the filling material often has shortcomings such as cracking, powder falling, and unsightly appearance, and rainwater can easily enter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/36C04B28/06
CPCC04B28/06Y02W30/91C04B14/06C04B14/28C04B14/308C04B16/0633C04B16/0658C04B16/0683C04B18/24C04B24/005C04B24/02C04B24/06C04B24/223C04B24/2623C04B24/2641C04B24/2688C04B24/383C04B24/42C04B2103/0085C04B2103/22C04B2103/302C04B2103/65C04B2103/69
Inventor 田凤兰段文峰韩朝辉
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap