Surface strengthened substrate, and preparation method thereof

A surface strengthening and matrix technology, applied in chemical instruments and methods, ion implantation plating, coating, etc., can solve problems such as high residual stress, high brittleness, surface strengthening failure, etc.

Inactive Publication Date: 2014-03-26
HONG FU JIN PRECISION IND (SHENZHEN) CO LTD +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in practical applications, the strengthening films such as chromium nitride film and chromium carbide film have disadvantages such as high brittleness, high residual stress, and poor bonding force with the substrate, and they are all simple substance strengthening films.
Therefore, as the thickness of the film increases and the temperature increases, these elemental strengthened films will have a large columnar crystal structure, which is prone to brittle cracks and peeling off, making the surface strengthening ineffective.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface strengthened substrate, and preparation method thereof
  • Surface strengthened substrate, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0015] See figure 1 , the embodiment of the present invention provides a surface strengthening base 100 , the surface strengthening base 100 includes a base 10 and a strengthening film 20 disposed on the surface of the base 10 .

[0016] The base 10 can be the body or casing of various products, such as molds, blades, casings of various electronic products, and the like. The base 10 includes metal bases such as magnesium bases, aluminum bases, and steel bases, and also includes composite material bases containing metal materials. In this embodiment, the base 10 is a steel base.

[0017] The strengthening film 20 is used to cover the surface of the base 10 to isolate the surface of the base 10 from the environment, and increase the hardness of the surface of the base 10 to effectively protect the base 10 . The thickness of the reinforcement film 20 c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A surface hardened substrate includes a base, a transition layer disposed on a surface of the base, and a hard layer disposed on the transition layer. The transition layer includes at least two kinds of transition metals. The hard layer includes an alloy and a nonmetal. The alloy includes the at least two kinds of transition metals.

Description

technical field [0001] The invention relates to a surface strengthening matrix and a preparation method of the surface strengthening matrix. Background technique [0002] In order to protect some substrates, such as watch cases, spectacle frames, mobile phones, computers, etc. from damage, a strengthening film is often provided on the surface of these substrates to form a surface strengthening substrate. Transition metal nitrides such as chromium nitride or transition metal carbides such as chromium carbide are often used to directly form the strengthening film on the surface of the substrate due to their high hardness, high friction and wear resistance and good chemical stability. However, in practical applications, the strengthening films such as chromium nitride film and chromium carbide film have disadvantages such as high brittleness, high residual stress, and poor bonding force with the matrix, and all of them are simple substance strengthening films. Therefore, as th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/01B32B9/04C23C14/35C23C14/06
CPCC22C19/03C23C14/0036C23C14/0635C22C27/06B32B15/01Y10T428/12493Y10T428/12535Y10T428/12778Y10T428/12944