Process for preparing spherical nanometer spinel zaffre by hydrothermal method

A technology of nano-spinel and hydrothermal method, which is applied in the field of preparation of spherical nano-spinel-type cobalt blue material by hydrothermal method, which can solve the problems of limited application range, complex synthesis process, and high price, and achieve a single shape , The process is simple, the effect of no pollution to the environment

Inactive Publication Date: 2011-11-16
JINGDEZHEN CERAMIC INSTITUTE
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

High-performance spherical nano-cobalt blue material still needs to be imported, but due to its complex synthesis process and high energy consumption, it is expensive, which limits its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing spherical nanometer spinel zaffre by hydrothermal method
  • Process for preparing spherical nanometer spinel zaffre by hydrothermal method
  • Process for preparing spherical nanometer spinel zaffre by hydrothermal method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) With cobalt chloride and aluminum chloride as raw materials, 0.15mol Co 2+ , 0.3mol Al 3+ Weigh it into a beaker, add deionized water, and then put the beaker on a magnetic stirrer and stir evenly;

[0033] (2) Slowly drop 3 mol / L NaOH solution into the uniformly stirred mixed solution, and continue stirring at a constant temperature of 20°C for 30 minutes until the pH of the solution is 13;

[0034] (3) Take a small amount of the supernatant of the above solution and add dropwise a few drops of 3mol / L NaOH solution to observe whether there is precipitation or not. If there is no precipitation, the reaction is complete;

[0035] (4) In the above-mentioned fully reacted solution, add a triethanolamine liquid with a volume fraction of 4% and a glycerol liquid with a volume fraction of 2%, and continue stirring for 30 minutes;

[0036] (5) Put the above-mentioned uniformly stirred mixed solution into a 100mL reactor with a filling degree of 70%, and incubate it under...

Embodiment 2

[0039] (1) With cobalt chloride and aluminum chloride as raw materials, 0.12mol Co 2+ , 0.24mol Al 3+ Add to the beaker, add deionized water, then put the beaker on a magnetic stirrer and stir evenly;

[0040] (2) Slowly drop 3 mol / L NaOH solution into the uniformly stirred mixed solution, and continue stirring at a constant temperature of 20°C for 30 minutes until the pH of the solution is 13;

[0041] (3) Take a small amount of the supernatant of the above solution and add dropwise a few drops of 3mol / L NaOH solution to observe whether there is precipitation or not. If there is no precipitation, the reaction is complete;

[0042] (4) In the above-mentioned fully reacted solution, add a triethanolamine liquid with a volume fraction of 8% and a glycerol liquid with a volume fraction of 4%, and continue stirring for 30 min;

[0043] (5) Put the above-mentioned uniformly stirred mixed solution into a 100mL reactor at a filling degree of 70%, and incubate it under hydrothermal ...

Embodiment 3

[0046] (1) With cobalt chloride and aluminum chloride as raw materials, 0.18mol Co 2+ , 0.36mol Al 3+ Add to the beaker, add deionized water, then put the beaker on a magnetic stirrer and stir evenly;

[0047] (2) Slowly drop 3 mol / L NaOH solution into the uniformly stirred mixed solution, and continue stirring at a constant temperature of 20°C for 30 minutes until the pH of the solution is 13;

[0048] (3) Take a small amount of the supernatant of the above solution and add dropwise a few drops of 3mol / L NaOH solution to observe whether there is precipitation or not. If there is no precipitation, the reaction is complete;

[0049] (4) In the above-mentioned fully reacted solution, add a triethanolamine liquid with a volume fraction of 12% and a glycerol liquid with a volume fraction of 6%, and continue stirring for 30 minutes;

[0050] (5) Put the above-mentioned uniformly stirred mixed solution into a 100mL reactor with a filling degree of 70%, and incubate it with hydroth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a process for preparing spherical nanometer spinel zaffre by the hydrothermal method. The process comprises the following steps: weighing and putting cobalt chloride and aluminum chloride according to a mol ratio of Co<2+> : Al <3+> = 1:2, putting the materials into a beaker, adding a proper amount of deionized water and carrying out uniform stirring on a magnetic stirrer;adding a sodium hydroxide solution drop by drop until the pH value of the mixture in the beaker is 13 and continuing stirring; adding mixed liquor of triethanolamine and glycerol with a volume fraction of 6 to 18% and resuming stirring; carrying out hydrothermal cultivation on the mixed solution at a temperature of 245 DEG C for 20 to 40 hours and taking the mixed solution out for natural coolingat room temperature; repeatedly rinsing the hydrothermal cultivation resultant material in liquid phase until the pH value equals 7 and putting the resultant material into a baking oven for drying attemperature of 60 DEG C so as to obtain spherical products with particle size less than 100 nm. The advantages of the invention are as follows: liquid phase hydrothermal cultivation is employed and composite organic matters are added; therefore, nanometer spherical powder is formed directly without calcining, energy consumption is relatively low, and no environmental pollution is generated.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a method for preparing spherical nano-spinel-type cobalt blue material by a hydrothermal method. Background technique [0002] Blue is one of the three primary colors of red, green and blue, and many colors are indispensable. In the decoration of ceramics, cobalt blue is an important spinel-type colored inorganic pigment, which is a composite oxide with a spinel structure. In a broad sense, the spinel-type composite oxide is the sum of the positive oxidation values ​​of the cations in its simplest formula is +8, while the negative oxidation value -8 is provided by four -2 oxygens. A class of composite oxides. For example, cobalt blue with the simplest chemical formula can be expressed by the following formula: CoAl 2 o 4 , also known as cobalt aluminate blue. [0003] Compared with other blue pigments, spinel-type cobalt blue pigment has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/85
Inventor 曹春娥胡琪陈云霞卢希龙余峰沈华荣洪琛
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com