X80 steel, low-temperature-resistant pipe fitting manufactured from X80 steel and manufacturing method of pipe fitting
A technology of low temperature resistance and manufacturing method, which is applied in the direction of manufacturing tools, furnace types, furnaces, etc., can solve the problems of pipe fittings not having low temperature resistance, achieve toughness and plasticity improvement, high and low temperature toughness impact performance, and improve hardenability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0020] Example 1:
[0021] The content of each element in a kind of X80 steel according to mass percentage is:
[0022] C 0.05 Si 0.1 Mn 1.2
[0023] Ni 0.6 Cr 0.08 Cu 0.05
[0024] Mo 0.1 Nb 0.03 The balance is Fe.
[0025] A tee with a diameter of 406mm and a thickness of 15mm is made.
[0026] The production method is as follows: use steel plate reel, use high Ni welding wire after welding, use mold hot pressing forming, welding wire contains 2.5% Ni, and the forming temperature is 800℃. After the pipe is formed, the quenching and tempering process is finally adopted, and the quenching temperature is 900 ℃, tempering temperature is 520, cooling rate is greater than 15℃ / s.
[0027] Composition of welding wire mass percentage:
[0028] C 0.06 Si 0.1 Mn 0.9
[0029] P 0 S 0 Ni 2.5
[0030] Mo 0 Cr 0 Cu 0
[0031] The remainder of V 0 Ti 0 B 0 is Fe.
[0032] The diameter of the welding wire is 2.0mm.
Example Embodiment
[0033] Example 2:
[0034] The content of each element in a kind of X80 steel according to mass percentage is:
[0035] C 0.1 Si 0.3 Mn 1.9
[0036] P 0.015 S 0.01 Al 0.05
[0037] Ni 3.5 Cr 0.4 Cu 0.3
[0038] V 0.05 Nb 0.1 Mo 0.35
[0039] Ti 0.02 B 0.001 The balance is Fe.
[0040] An elbow with a diameter of 1422mm and a thickness of 60mm is made.
[0041] The production method is as follows: use steel plate reel, use high Ni welding wire and then use mold hot pressing forming, the Ni content of the wire is 3.6%, the forming temperature is 1000 ℃, and the pipe fittings are finally formed by quenching and tempering process, the quenching temperature is 1050 ℃, tempering temperature is 650℃, cooling rate is greater than 15℃ / s.
[0042] Composition of welding wire mass percentage:
[0043] C 0.1 Si 0.35 Mn 1.5
[0044] P 0.016 S 0.01 Ni 3.6
[0045] Mo 0.5 Cr 0.1 Cu 0.3
[0046] V 0.1 Ti 0.1 B 0.1 The balance is Fe.
[0047] The diameter of the welding wire is 4.2mm.
Example Embodiment
[0048] Example 3:
[0049] The content of each element of a kind of X80 according to mass percentage is:
[0050] C 0.75 Si 0.2 Mn 1.5
[0051] P 0.008 S 0.005 Al 0.025
[0052] Ni 2 Cr 0.2 Cu 0.15
[0053] V 0.025 Nb 0.05 Mo 0.2
[0054] Ti 0.01 B 0.0005 The balance is Fe.
[0055] A tee with a diameter of 800mm and a thickness of 30mm is made.
[0056] The production method is as follows: use steel plate reel, use high Ni welding wire and then use mold hot pressing forming. The Ni content of the wire is 3%, and the forming temperature is 900℃. After the pipe is formed, the quenching and tempering process is finally adopted, and the quenching temperature is 1000. ℃, tempering temperature 600℃, cooling rate greater than 15℃ / s.
[0057] Composition of welding wire mass percentage:
[0058] C 0.08 Si 0.2 Mn 1.2
[0059] P 0.012 S 0.008 Ni 3
[0060] Mo 0.25 Cr 0.05 Cu 0.15
[0061] V 0.005 Ti 0.005 B 0.0005
[0062] The balance is Fe.
[0063] The diameter of the welding wire is 3mm.
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap