Preparation method of stainless steel bearing steel pipe and ferrule

A technology for bearing steel pipes and bearing rings, applied in the field of preparation of stainless steel bearing rings, can solve the problems of low production efficiency of processing stainless steel bearing rings, stainless steel bearing rings, low yield of round steel bars, etc. Effect

Inactive Publication Date: 2011-12-07
张家港市逸洋制管有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the particularity of the stainless steel material, the current stainless steel bearings can only be turned by round steel rods, and then stamped into rings. The traditional perforated pipe making process cannot be used to process stainless steel bearing rings, which makes the yield of round steel rods very high. Low, low production efficiency of stainless steel bearing rings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Specific embodiments of the present invention are described in detail below.

[0015] The method for preparing the stainless steel bearing steel pipe of the present invention includes the following steps:

[0016] 1) Heating perforation: heat the round bar material of 3Cr13 to 1040~1070℃, keep it for 20~30 minutes, and perforate at the speed of 10~18m / min to obtain the tube blank;

[0017] 2) Isothermal annealing: heat the tube to 830~850℃, keep it for 2~3 hours, then cool to 700~720℃ at a cooling rate of less than 30℃ per hour, and then at a cooling rate of less than 50℃ per hour Baked

[0018] 3) Rolling: heat the annealed billet to 250~300℃, and then roll it to the bearing steel pipe of the specified size at a speed of 7~8mm per minute;

[0019] 4) Stress relief annealing: The rolled bearing steel pipe is heated to 760~780℃ within 0.6~1 hour, kept for 2~3 hours, and then discharged at a cooling rate of less than 50℃ per hour.

[0020] In this embodiment, in order to pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a stainless steel bearing steel tube. The method can improve yield and production efficiency and comprises the steps of: 1) heating and perforating: heating a round bar to 1,040 DEG C-1,070 DEG C, carrying out thermal insulation for 20-30 minutes, perforating at a speed of 10-18 meters per minute, thus obtaining a tube blank; 2) annealing at equal temperature: heating the tube blank to 830-850 DEG C, carrying out thermal insulation for 2-3 hours, then cooling to 700-720 DEG C at a cooling speed less then 30 DEG C per hour, and then discharging under the condition that a cooling speed is less than 50 DEG C per hour; 3) rolling: heating the annealed tube blank to 250-300 DEG C, and then rolling the annealed tube blank into a bearing steel tubewith a given size at a speed of 7-8mm per minute; and 4) stress relief annealing: increasing the temperature of the rolled bearing steel tube to 760-780 DEG C, carrying out thermal insulation for 2-3hours, then discharging under the condition that a cooling speed is less than 50 DEG C per hour. By adopting the preparation method, the stainless steel round bar made from 3Cr13 can be manufactured into the bearing steel tube meeting the requirement.

Description

Technical field [0001] The invention relates to a method for preparing a bearing ring, in particular to a method for preparing a stainless steel bearing ring. Background technique [0002] With the widespread application of maintenance-free technology, stainless steel bearings have been widely used in food machinery, daily-use machinery and various corrosion-resistant fields. Due to the particularity of the stainless steel material, the current stainless steel bearings can only be turned by round steel rods and then stamped complete sets of rings. The traditional perforated pipe making process cannot be used to process stainless steel bearing rings. This makes the yield rate of round steel rods very high. Low, the production efficiency of stainless steel bearing rings is low. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing a stainless steel bearing steel pipe which can improve the yield rate and pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
Inventor 罗志钢徐卫新陈文元朱雪峰张秋
Owner 张家港市逸洋制管有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap