Yellow high-gloss glaze material for ceramics and preparation method thereof

A yellow and glaze technology, applied in the field of yellow glaze and its preparation, yellow high-gloss glaze for ceramics and its preparation, can solve the problems of yellow glaze color, brightness and vividness are not very good, there is luster, etc., and achieve glossiness Good, pure color, stable hair effect

Active Publication Date: 2013-08-07
CHAOZHOU QINGFA CERAMICS
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the color, brightness and vividness of yellow glazes on the market are not very good. Only the high-end art porcelain has better enamel quality. The yellow glazes in daily-use porcelains have problems such as luster, which urgently need to be solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A yellow high-gloss glaze for ceramics and a preparation method thereof:

[0018] 30 parts of potassium feldspar, 20 parts of quartz, 5 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, 1 part of cerium oxide, 1 part of niobium oxide, 4 parts of yellow pigment and 50 parts of water;

[0019] (1) Mix 30 parts of potassium feldspar, 20 parts of quartz, 5 parts of marble, 8 parts of kaolin, 6 parts of transparent frit, and 50 parts of water evenly, ball mill for 15 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0020] (2) Mix 1 part of cerium oxide, 1 part of niobium oxide and 4 parts of yellow pigment evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0021] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain a yellow high-gloss glaze for ceramics.

Embodiment 2

[0023] A yellow high-gloss glaze for ceramics and a preparation method thereof:

[0024] 40 parts of potassium feldspar, 32 parts of quartz, 10 parts of marble, 12 parts of kaolin, 6 parts of transparent frit, 2 parts of cerium oxide, 2 parts of niobium oxide, 6 parts of yellow pigment and 60 parts of water;

[0025] (1) Mix 40 parts of potassium feldspar, 32 parts of quartz, 10 parts of marble, 12 parts of kaolin, 6 parts of transparent frit, and 60 parts of water evenly, ball mill for 17 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0026] (2) Mix 2 parts of cerium oxide, 2 parts of niobium oxide and 6 parts of yellow pigment evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0027] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain a yellow high-gloss glaze for ceramics.

Embodiment 3

[0029] A yellow high-gloss glaze for ceramics and a preparation method thereof:

[0030] 35 parts of potassium feldspar, 25 parts of quartz, 8 parts of marble, 10 parts of kaolin, 9 parts of transparent frit, 3 parts of cerium oxide, 3 parts of niobium oxide, 8 parts of yellow pigment and 70 parts of water;

[0031] (1) Mix 35 parts of potassium feldspar, 25 parts of quartz, 8 parts of marble, 10 parts of kaolin, 9 parts of transparent frit, and 55 parts of water evenly, ball mill for 16 hours, and the fineness reaches 325 mesh, and the obtained glaze is used for later use;

[0032] (2) Mix 3 parts of cerium oxide, 3 parts of niobium oxide and 8 parts of yellow color evenly, ball mill until the fineness reaches 325 mesh, and set aside;

[0033] (3) Mix the materials obtained in step (1) and step (2) evenly to obtain a yellow high-gloss glaze for ceramics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a yellow high-gloss glaze material for ceramics, which is prepared from 30-50 parts of potash feldspar, 20-40 parts of quartz, 5-15 parts of marble, 8-15 parts of kaolin, 6-10 parts of clear frit, 1-4 parts of ceria, 1-4 parts of niobium oxide, 4-12 parts of yellow pigment and 50-70 parts of water. The preparation method comprises the following steps: evenly mixing the 30-50 parts of potash feldspar, 20-40 parts of quartz, 5-15 parts of marble, 8-15 parts of kaolin, 6-10 parts of clear frit and 50-70 parts of water, and carrying out ball milling for 15-20 hours until the fineness reaches 325 meshes; evenly mixing the 1-4 parts of ceria, 1-4 parts of niobium oxide and 4-12 parts of yellow pigment, and carrying out ball milling until the fineness reaches 325 meshes;and finally, evenly mixing the two mixtures to obtain the yellow high-gloss glaze material for ceramics. The glaze material has the advantages of favorable combination performance with the green body, pure and bright color, high stability and high gloss.

Description

technical field [0001] The invention relates to a yellow glaze and a preparation method thereof, in particular to a yellow high-gloss glaze for ceramics and a preparation method thereof, belonging to the technical field of ceramic glaze production. Background technique [0002] Yellow glaze occupies a very important position in ancient ceramic art. Yellow has always been a special color for emperors. In ancient times, folks were not allowed to use it. Therefore, there are not many porcelains that use yellow glaze. With the development of society, yellow glaze gradually entered the folk. Used by ordinary people, it has become a bright color in daily-use porcelain. [0003] At present, the yellow glazes on the market are not very good in color, brightness and vividness. Only the high-end art porcelain has better enamel. The yellow glazes in daily-use porcelains have some problems such as luster, which urgently need to be solved. Contents of the invention [0004] The pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 蔡金元
Owner CHAOZHOU QINGFA CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com