A low-alloy, high-strength steel technology, which is applied in the direction of metal material coating process, coating, solid-state diffusion coating, etc., can solve the problem that affects the dimensional accuracy of products, and the 15CrMo heat-resistant high-strength steel is difficult to meet the toughness and creep of industrial equipment. , weldability and other issues, to achieve the effect of small deformation and excellent high temperature performance

Inactive Publication Date: 2012-06-20
宁波市博祥新材料科技有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the rapid development of modern industry, 15CrMo heat-resistant high-strength steel has become increasingly difficult to meet the higher requirements of industrial equipment in terms of strength, toughness, creep, weldability, etc., optimize alloy composition, adjust smelting, rolling and other production Process parameters in engineering have increasingly become the focus of people's attention to improving 15CrMo steel
At the same time, in order to obtain the required excellent wear resistance and fatigue resistance, it is necessary to perform heat treatment such as carburizing and quenching, which often causes a certain deformation of the product and affects the dimensional accuracy of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Hereinafter, the present invention will be described in detail through specific examples.

[0030] A low-alloy heat-resistant high-strength steel and components thereof, which are prepared through the following steps,

[0031] First, design the composition of the low-alloy heat-resistant high-strength steel, in weight percentage (%), including: C 0.1, Si 0.1, Mn 0.2, Cr 1.2, Mo 0.4, P 0.009, S 0.006, Ni 0.3 , Cu 0.05, V 0.35, Nb 0.15, W 0.3, Ti 0.01, the balance is Fe and unavoidable impurities;

[0032] Second, smelting and pouring, including electric arc furnace primary smelting, ladle RH treatment and LF treatment, control the molten steel to meet the chemical composition requirements before pouring, in which argon is blown at a pressure of 5atm for 5 minutes during ladle refining to facilitate the floating and removal of impurities ;

[0033] Third, rolling, including soaking treatment, rolling and cooling, wherein soaking treatment is soaking in a heating furnace...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a member with superior high temperature performance and small deformation, which is prepared by rationally optimizing components of the steel and controlling parameters of preparation processes such as smelting, rolling and thermal treatment on the basis of 15CrMo, wherein the room temperature tensile strength of the member is 610 MPa; the effective life of the member is twice that of 15CrMo through stress test of 600 DEG C and 200 MPa; the application temperature of the heat-resistant steel is obviously improved; the surface hardness after thermal treatment is 750 HV;the thickness of a hard layer with the hardness over 500 HV is 0.5 mm; the deformation is small; the welding property is also extremely excellent; and the member exceeds 15CrMo in all aspects.

Description

technical field [0001] The invention relates to a steel material and its components, in particular to a low-alloy heat-resistant high-strength steel and its components. Background technique [0002] Under high temperature conditions (usually refers to the temperature above 0.3-0.5 times the melting point of the material), the steel with oxidation resistance, sufficient high temperature strength and good heat resistance is called heat-resistant steel, and the most representative of heat-resistant steel One is low-alloy heat-resistant high-strength steel. For example, 15CrMo in my country is a typical low-alloy heat-resistant high-strength steel. 15CrMo is widely used in boilers, petroleum Pipelines, containers, components, etc. of large-scale equipment with harsh service conditions and complex corrosive media such as chemical industry, coal conversion, steam turbine cylinder block, thermal power, and nuclear power. [0003] However, with the rapid development of modern industr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/50C21C7/072C21D8/00C21D1/18C23C8/22C23F17/00
Inventor 杨学焦
Owner 宁波市博祥新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap