Boron-contained centrifugal composite high-speed steel roller and manufacturing method thereof

A centrifugal composite, high-speed steel technology, applied in the direction of rolls, metal rolling, metal rolling, etc., can solve the problems of low strength of ductile iron, poor composite ability of the outer layer of the roll and the core of the roll, easy to peel, etc., to achieve hardness High strength, strong accident resistance, not easy to peel off

Inactive Publication Date: 2012-08-01
常熟市轧辊厂有限公司
View PDF7 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing production technology, what the outer layer of the roll adopts is high-speed steel, and what the core of the roll adopts is ductile iron. The strength of ductile iron in the lower part is ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron-contained centrifugal composite high-speed steel roller and manufacturing method thereof
  • Boron-contained centrifugal composite high-speed steel roller and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The preferred embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0025] The invention provides a boron-containing centrifugal composite high-speed steel roll, which comprises a high-speed steel roll outer layer, a high-speed steel roll middle layer and a high-speed steel roll core. The weight percent of the chemical composition of the outer layer of the high-speed steel roll in the present invention is: C: 0.8-0.9%, Si: 1.0-1.2%, Mn: 0.9-1.2%, P: ≤0.03%, S: ≤0.03%, Ni : 0.9-1.0%, Cr: 5-6%, Mo: 1.4-1.5%, B: 1.9-2.2%, V: 1.4-1.6%, W: 2-3%, Nb: 0.4-0.5% and rare earth; The weight percent of the chemical composition of the middle layer of the high-speed steel roll is: C: 1.7-1.8%, Si: 1.4-1.6%, Mn: 0.9-1.0%, P: ≤0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a boron-contained centrifugal composite high-speed steel roller, which comprises an outer layer of the high-speed steel roller, a middle layer of the high-speed steel roller and a core of the high-speed steel roller. The manufacturing method includes steps of smelting, interrupted front treatment, roller pouring, annealing, rough machining, double tempering, finish machining and testing. By the method, three-layer composite roller technology is adopted in the boron-contained centrifugal composite high-speed steel roller, composite ability of the outer layer of the high-speed steel roller and the core of the high-speed steel roller is increased, the roller is less prone to spalling, high in rigidity and accident resistant ability, fine in abrasion resistance, safe in use, low in energy consumption and short in cycle in heat treatment, oxidation and decarburization of the roller and roller breakage in use are avoided. The manufacturing method is simple and hot quenching process is omitted.

Description

technical field [0001] The invention relates to the technical field of composite steel rolls, in particular to a boron-containing centrifugal composite high-speed steel roll and a preparation method thereof. Background technique [0002] With the rapid development of the metallurgical industry, my country's current annual output of rolled products is close to 670 million tons, accounting for about 50% of the world's total rolled products, and modern rolling technology generally uses low-temperature rolling and endless continuous rolling And other advanced rolling technology. The roll is a key component that is consumed in large quantities in steel rolling production. Therefore, high requirements are put forward for the performance and service life of the roll. The composite high-speed steel roll is widely used in the steel rolling industry for its high hardness, good wear resistance and excellent use effect. widely adopted and respected. [0003] High-speed steel roll is a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B27/00C22C38/54C22C38/56C22C37/10B22D13/02
Inventor 冯文华浦小弟严志成
Owner 常熟市轧辊厂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap