Coconut fiber plate for mattress

A coconut palm board and mattress technology, which is applied in mattresses, spring mattresses, applications, etc., can solve the problems of uneven thickness, pungent, uneven mattress surface, etc., so that it is not easy to be affected by moisture and mildew, and has no glue smell , no formaldehyde release effect

Active Publication Date: 2012-09-19
昆山吉美川纤维科技有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 1. The content of formaldehyde seriously exceeds the standard, and the user inhales it into the body during sleep, causing harm to the body;
[0006] 2. The smell of glue is strong and pungent, and users are prone to allergic reactions;
[0007] 3. The glue will be mildewed and wormy when it is damp, and long-term use is not good for the body;
[0008] 4. It is easy to break, the glue is hard, the sun will be exposed to the sun, and it will be severely deformed in freezing weather
[0009] 5. The surface of the mattress is uneven and the thickness is uneven

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The coconut palm board used for mattresses of this embodiment comprises an upper layer, a middle layer and a lower layer compounded together by hot air penetration technology, and the upper layer and the lower layer are mixtures of two-component sheath-core fibers and polyester hollow fibers, and the upper layer and the lower layer The content of the two-component sheath-core fiber by weight in the middle layer is 30%, and the middle layer is a mixture of the two-component sheath-core fiber and coconut palm fiber, and the content of the two-component sheath-core fiber by weight in the middle layer is 20%. .

[0043] The sheath of the two-component sheath-core fiber is a PET material with a melting point of 100°C, the core is a PET material with a melting point of 254°C, and the weight ratio of the sheath to the core is 1:1. The polyester hollow fiber is a PET material with a melting point of 265°C and a hollowness of 75%.

[0044] The diameter of the coconut palm fiber...

Embodiment 2

[0057]The coconut palm board used for mattresses of this embodiment comprises an upper layer, a middle layer and a lower layer compounded together by hot air penetration technology, and the upper layer and the lower layer are mixtures of two-component sheath-core fibers and polyester hollow fibers, and the upper layer and the lower layer The content of the two-component sheath-core fiber by weight in the middle layer is 50%, and the middle layer is a mixture of two-component sheath-core fiber and coconut palm fiber, and the content of the two-component sheath-core fiber by weight in the middle layer is 40%. .

[0058] The sheath of the two-component sheath-core fiber is a PET material with a melting point of 119°C, the core is a PET material with a melting point of 264°C, and the weight ratio of the sheath to the core is 1:4. The polyester hollow fiber is a PET material with a melting point of 265°C and a hollowness of 85%.

[0059] The diameter of the coconut palm fiber is 0...

Embodiment 3

[0072] The coconut palm board used for mattresses of this embodiment comprises an upper layer, a middle layer and a lower layer compounded together by hot air penetration technology, and the upper layer and the lower layer are mixtures of two-component sheath-core fibers and polyester hollow fibers, and the upper layer and the lower layer The content of the two-component sheath-core fiber by weight in the middle layer is 35%, and the middle layer is a mixture of two-component sheath-core fiber and coconut palm fiber, and the content of the two-component sheath-core fiber by weight in the middle layer is 30%. .

[0073] The sheath of the two-component sheath-core fiber is a PET material with a melting point of 121° C., the core is a PET material with a melting point of 260° C., and the weight ratio of the sheath to the core is 1:4. The polyester hollow fiber is a PET material with a melting point of 264°C and a hollowness of 85%.

[0074] The diameter of the coconut palm fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a coconut fiber plate, in particular to a coconut fiber plate for a mattress, which comprises an upper layer, a middle layer and a lower layer which are compounded together through a hot air penetrating technology, wherein the upper layer and the lower layer comprise dual-component sheath core fibers and polyester hollow fibers, and the middle layer comprises dual-component sheath core fibers and coconut fibers. The coconut fiber plate for the mattress has the advantages of no formaldehyde release, no glue smell, difficulty in dampness and mildew, flat surface and uniformity in thickness.

Description

technical field [0001] The invention relates to household articles, in particular to a coconut palm board for a mattress. Background technique [0002] The coconut palm board used for mattresses in the prior art uses a large amount of glue to bond the palm board, and the formaldehyde seriously exceeds the standard, which is seriously harmful to the human body. The coconut palm board in the prior art is used as a mattress auxiliary material, which is suitable for hard mattresses; the glue is bonded to the coconut palm, the formaldehyde in the glue exceeds the standard, the smell is strong, it is easy to mold, it is easy to be damp and deteriorated by insects, easy to collapse, and easy to break. [0003] In the existing preparation process of coconut palm boards for mattresses, a large amount of toxic glue is used to reduce the cost of forming boards. Coconut palm silk and glue are bonded and molded. Laying net - glue spraying - hot pressing forming - trimming. This kind of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A47C27/12B32B9/02B32B27/02B32B27/36
Inventor 李中勇
Owner 昆山吉美川纤维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com