Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Cold-resistant and pressure-resistant PVC (polyvinyl chloride) profiled bar

A profile and pressure-resistant technology, which is applied in the field of cold-resistant and pressure-resistant PVC profiles, can solve problems such as fragility, increase the quality of PVC, and heavy profiles, so as to enhance cold resistance and bending resistance, and strengthen bonding Affinity, performance-enhancing effects

Inactive Publication Date: 2012-09-12
新疆蓝山屯河型材有限公司 +1
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current PVC profiles are heavy, low in strength, poor in cold resistance, and easily shattered
In view of the above shortcomings of PVC profiles, there are also many technologies to solve them. Generally, an additional layer is wrapped outside the PVC profile or other materials are implanted inside the PVC profile. However, this will increase the quality of PVC and prepare The process is complicated and causes a lot of waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A cold-resistant and pressure-resistant PVC profile, comprising a PVC substrate, a processing enhancer, and a PVC modified agent, the content of the PVC substrate is 60%, the content of the processing enhancer is 5%, the PVC modified agent The content is 35%, of which,

[0016] The weight ratio of the PVC substrate component is: polyvinyl chloride, 100KG; A050-T, 2KG; antimony trioxide, 15-20KG; octyl tin mercaptan, 2KG; epoxy soybean oil, 5- 7KG; Zinc stearate, 0.5KG; Stearic acid, 0.5KG;

[0017] The weight ratio of the processing enhancer is: modified PVC resin, 3KG; nano calcium carbonate, 5-10KG; adhesion promoter, 0.5KG; processing aid, 2KG; titanium dioxide, 10KG; methyl methacrylate Ester-butadiene-styrene copolymer, 5-10 KG;

[0018] The weight ratio of the components of the PVC modified formulation is: ethylene-vinyl acetate copolymer (EVA), 2KG; dioctyl phthalate (DOP), 2.5KG; cyclohexanone, 4KG; xylene, 5KG.

Embodiment 2

[0020] A cold-resistant and pressure-resistant PVC profile, comprising a PVC base material, a processing enhancer and a PVC modified agent, the content of the PVC base material is 70%, the content of the processing enhancer is 5%, the PVC modified agent The content is 25%, of which,

[0021] The weight ratio of the PVC substrate component is: polyvinyl chloride, 100KG; A050-T, 2KG; antimony trioxide, 15-20KG; octyl tin mercaptan, 2KG; epoxy soybean oil, 5- 7KG; zinc stearate, 0.5KG; stearic acid, 0.5KG; processing aid, 2KG; titanium dioxide, 10KG;

[0022] The weight ratio of the processing enhancer is: modified PVC resin, 5KG; nano calcium carbonate, 5-10KG; adhesion promoter, 0.5KG; processing aid, 2 parts; titanium dioxide, 10 parts; methyl Methyl acrylate-butadiene-styrene copolymer, 5-10KG;

[0023] The weight ratio of the components of the PVC modified formulation is: ethylene-vinyl acetate copolymer (EVA), 3 KG; dioctyl phthalate (DOP), 3 KG; cyclohexanone, 4 KG; xylene, 5K...

Embodiment 3

[0025] A cold-resistant and pressure-resistant PVC profile, comprising a PVC base material, a processing enhancer and a PVC modified agent, the content of the PVC base material is 70%, the content of the processing enhancer is 5%, the PVC modified agent The content is 25%, of which,

[0026] The weight ratio of the PVC substrate components is: polyvinyl chloride, 100KG; ACR401, 2KG; antimony trioxide, 15-20KG; methyl tin mercaptan, 2KG; epoxy soybean oil, 5-7KG; Zinc stearate, 0.5KG; stearic acid, 0.5KG; processing aid, 2KG; titanium dioxide, 10KG;

[0027] The weight ratio of the processing enhancer is: modified PVC resin, 6.5KG; nano calcium carbonate, 5-10KG; adhesion promoter, 0.5KG; processing aid, 2 parts; titanium dioxide, 10 parts; Methyl acrylate-butadiene-styrene copolymer, 5-10KG;

[0028] The weight ratio of the components of the PVC modified formulation is: ethylene-vinyl acetate copolymer (EVA), 3.5 KG; dioctyl phthalate (DOP), 3.5 KG; cyclohexanone, 4 KG; xylene , 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cold-resistant and pressure-resistant PVC (polyvinyl chloride) profiled bar which comprises a PVC base material, a processing reinforcing agent and a PVC modifying agent. The content of the PVC base material ranges from 60% to 85%, the content of the processing reinforcing agent ranges from 3% to 7%, and the content of the PVC modifying agent ranges from 10% to 35%. The PVC base material is composed of, by weight, 100 parts of polyvinyl chloride, 2 parts of antioxidants, 15-20 parts of flame retardants, 2 parts of heat stabilizers, 5-7 parts of epoxidized soybean oil, 0.5 part of zinc stearate, 0.5 part of stearic acid, 2 parts of processing agents and 10 parts of titanium dioxide. The PVC modifying agent is composed of, by weight, 2-5 parts of ethylene-ethylene vinyl acetate copolymer, 2.5-4 parts of di-n octyl phthalate, 4 parts of cyclohexanone and 5 parts of dimethylbenzene. The cold resistance and the pressure resistance of the cold-resistant and pressure-resistant PVC profiled bar are greatly improved, the preparation process is simple, and materials are easily obtained.

Description

technical field [0001] The invention relates to a PVC profiled material, in particular to a cold-resistant and pressure-resistant PVC profiled material. Background technique [0002] With the continuous advancement of science and technology, the appearance of the city is changing with each passing day, and the urban construction is getting faster and faster, so the application of PVC profiles is becoming more and more extensive. However, the current PVC profiles are heavy, low in strength, poor in cold resistance, and easily shattered. In view of the above shortcomings of PVC profiles, there are also many technologies to solve them. Generally, an additional layer is wrapped outside the PVC profile or other materials are implanted inside the PVC profile. However, this will increase the quality of PVC and prepare The process is complicated and causes a lot of waste. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/22C08K5/58C08K5/524C08K5/1515C08K5/098C08K5/09C08K3/26C08L33/12C08L23/08C08K5/12
Inventor 潘竟军蒋文君冯军李自银翟玲张雪梅尚庆舂
Owner 新疆蓝山屯河型材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com