Hot forming method and hot forming mould

A thermoforming and mold technology, applied in the direction of forming tools, manufacturing tools, metal processing equipment, etc., can solve the problems of no smooth transition, prone to fracture, large performance differences, etc., to save production costs, improve design space, and simple structure Effect

Active Publication Date: 2012-09-19
HANGZHOU BRANCH ZHEJIANG GEELY AUTOMOBILE RES INST +2
View PDF9 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the properties of the two sides of the weld of the parts obtained by this me

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot forming method and hot forming mould
  • Hot forming method and hot forming mould
  • Hot forming method and hot forming mould

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] The content of the present invention will be described in detail below with reference to the drawings and specific embodiments.

[0021] figure 1 It is a schematic structural diagram of an embodiment of the thermoforming mold according to the present invention. The thermoforming mold has different cooling rates through different arrangement of cooling pipe densities in different regions. Such as figure 1 As shown, the thermoforming mold includes a mold base 1 in which a plurality of parallel longitudinal cooling pipes 2 are provided. In this figure, the cooling pipes of the three regions A, B, and C in the transverse direction of the thermoforming die are arranged from dense to sparse, so that the three regions corresponding to the thermoforming die A, B, and C can have different cooling rates. Among them, the cooling rate of zone A can be 75-90°C / s, the cooling rate of zone B can be 35-55°C / s, and the cooling rate of zone C can be 5-15°C / s. The steel plate is put in aft...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hot forming method and a hot forming mould. The hot forming method includes providing the hot forming mould which is provided at least with a first portion and a second portion long the horizontal direction; guiding a heated austenitized steel plate into the hot forming mould to be subjected to forming process; cooling the first portion of the hot forming mould at a first cooling rate and cooling the second portion of the hot forming mould at a second cooling rate, wherein the first cooling rate is different from the second cooling rate, accordingly, an integrally formed component with changed transverse strength is formed in the hot forming mould. The structure of the hot forming mould is simple, components with diversified originations and different strength distribution can be obtained through simple process, performances of different positions of the components can have great differences, so that requirements of different occasions can be satisfied. Due to the hot forming method, not only the design space of steel plate materials can be improved, but also parameter setting is simplified, and the production cost is reduced.

Description

technical field [0001] The invention relates to a thermoforming technology, in particular to a thermoforming method and a thermoforming mold. Background technique [0002] Hot forming technology is a latest manufacturing process that combines traditional hot forging technology with cold stamping technology, and is specially used to form high-strength stamping parts, which can form auto parts with a strength of up to 1500MPa. At present, thermoforming technology has become the focus of attention of many automobile manufacturers in the world. The hot forming technology is different from the traditional cold stamping forming process. The cold stamping forming is mostly carried out at room temperature, while in the hot forming technology, the sheet is stamped and formed in a red hot state, that is, the blanked steel plate is sent into the Heating in the heating device to make it austenitized, and then sending it to the hot forming mold with a cooling system inside for stamping....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21D37/10B21D37/16
Inventor 马宁门永新马芳武赵福全
Owner HANGZHOU BRANCH ZHEJIANG GEELY AUTOMOBILE RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap