Method for coloring surface of ceramic body and ceramic colorant

A technology for ceramic body and surface coloring, applied in the field of ceramic materials, can solve the problems of unclear concave and convex contours of the die surface, poor imitation stone effect, color limitation of glaze, etc., and achieve a realistic imitation stone effect, low cost and delicate texture. Effect

Active Publication Date: 2012-09-19
GUANGDONG NEWPEARL CERAMIC GRP CO LTD +1
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The surface coloring of the existing ceramic body is carried out by glazing, that is, a glaze layer is applied on the surface of the ceramic body. The glaze layer is usually thicker and the amount of glaze applied is relatively large. Taking a ceramic tile with a size of 45×95mm as an example, it requires 4.0 ~6.0 g / piece of glaze, so there are obvious glaze traces on the surface of the product, the uneven contour of the mold surface is not clear, the effect of imitating stone is poor, the color of the glaze is relatively limited, the process is more complicated, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for coloring surface of ceramic body and ceramic colorant
  • Method for coloring surface of ceramic body and ceramic colorant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Such as figure 1 Shown, the invention provides a kind of method for coloring the surface of ceramic body, the method comprises the steps:

[0044] 1. Preparation of ceramic body

[0045] Configure the green body raw materials, where K 2 O and Na 2 The content of O is controlled at 4.0% to 6.0% of the weight percentage of the total ceramic body raw material; K 2 O: Na 2 O=1:0.8~1:2; the CaO content is controlled below 1.5% by weight of the total ceramic body raw materials; the MgO content is controlled below 1.5% by weight of the total ceramic body raw materials.

[0046] Perform ball milling and pulping on the configured green body raw materials;

[0047] To test the mud;

[0048] Spray and granulate the slurry;

[0049] Detect the powder formed after granulation;

[0050] The qualified powder is pressed into a ceramic green body.

[0051] 2. Atomize and spray the coloring agent on the surface of the ceramic body. The raw materials of the coloring agent are tap...

Embodiment 2

[0067] 1. Preparation of ceramic body

[0068] Configure the green body raw materials, where K 2 O and Na 2 The content of O is controlled at 4.0% to 6.0% of the weight percentage of the total ceramic body raw material; K 2 O: Na 2 O=1:0.8~1:2; the CaO content is controlled below 1.2% by weight of the total ceramic body raw materials; the MgO content is controlled below 1.2% by weight of the total ceramic body raw materials.

[0069] Perform ball milling and pulping on the configured green body raw materials;

[0070] To test the mud;

[0071] Spray and granulate the slurry;

[0072] Detect the powder formed after granulation;

[0073] The qualified powder is pressed into a ceramic green body.

[0074] 2. Atomize and spray the colorant on the surface of the ceramic body. The raw materials of the colorant are factory circulating water, chemical materials, ceramic colorants and suspension stabilizers. The chemical materials are quartz and zirconium silicate, and the ceram...

Embodiment 3

[0086] 1. Preparation of ceramic body

[0087] Configure the green body raw materials, where K 2 O and Na 2 The content of O is controlled at 4.0% to 6.0% of the weight percentage of the total ceramic body raw material; K 2 O: Na 2 O=1:0.8~1:2; the CaO content is controlled below 1.0% by weight of the total ceramic body raw materials; the MgO content is controlled below 1.0% by weight of the total ceramic body raw materials.

[0088] Perform ball milling and pulping on the configured green body raw materials;

[0089] To test the mud;

[0090] Spray and granulate the slurry;

[0091] Detect the powder formed after granulation;

[0092] The qualified powder is pressed into a ceramic green body.

[0093] 2. Atomize and spray the colorant on the surface of the ceramic body. The raw materials of the colorant are river water, chemical materials, ceramic colorants and suspension stabilizers. The chemical materials are frits, and the ceramic colorants are water-insoluble color...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for coloring the surface of a ceramic body and a ceramic colorant. The method comprises the following steps of: (1) spraying the colorant on the surface of the ceramic body, wherein the raw materials of the colorant comprise water, a chemical material, a ceramic pigment and a suspension stabilizer, and the chemical material is one or a combination of a low-temperature bright flux, a high-temperature non-luminous material and an opacifier; (2) drying the ceramic body sprayed with the colorant; and (3) burning the dried ceramic body at a high temperature to obtain a product, wherein the raw materials of the colorant comprise water, a chemical material, a ceramic colorant and a suspension stabilizer. The used colorant disclosed by the invention mainly contains water, also contains a little of chemical material and ceramic pigment, and is sprayed on the surface of the ceramic body; the spraying amount is less; and the cost is very low and the process is very simple compared with the existing glazing method.. The colorant is sprayed on the surface of the ceramic body; the product can completely keep the modular surface effect of the ceramic body before being sprayed with the colorant; and concave and convex outlines of the modular surface are clearer and sharper, and the effect of imitating stone is vivid.

Description

technical field [0001] The invention relates to the field of ceramic materials, in particular to a method for coloring the surface of a ceramic body and a ceramic colorant. Background technique [0002] The surface coloring of the existing ceramic body is carried out by glazing, that is, a glaze layer is applied on the surface of the ceramic body. The glaze layer is usually thicker and the amount of glaze applied is relatively large. Taking a ceramic tile with a size of 45×95mm as an example, it requires 4.0 ~6.0 g / piece of glaze, so there are obvious glaze traces on the surface of the product, the uneven contour of the mold surface is not clear, the effect of imitating stone is poor, the color of the glaze is relatively limited, the process is relatively complicated, and the production cost is high. Contents of the invention [0003] The object of the present invention is to provide a new method for coloring the surface of ceramic bodies and the coloring agent used in thi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/85
Inventor 叶德林彭中华邹常彪
Owner GUANGDONG NEWPEARL CERAMIC GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More