Rubber composition with low calorification and low rolling resistance

A low rolling resistance, rubber composition technology, applied in the direction of rolling resistance optimization, road transportation emission reduction, etc., can solve problems such as damage of rubber products, accelerated thermal oxidation aging of rubber, etc., to achieve improved wet skid resistance, improved processing performance, Rolling resistance reduction effect

Active Publication Date: 2012-09-19
PINGDINGSHAN YICHENG NEW MATERIAL
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compression heat generation has a great influence on the performance of rubber products that need to be repeatedly deformed. If the compression heat generation is too large, the rubber product will heat up rapidly. The temperature rise not only accelerates the thermo-oxidative aging of rubber, but also may cause rubber products to deteriorate due to excessive temperature. the destruction of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber composition with low calorification and low rolling resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] A rubber composition with low heat generation and low rolling resistance, using natural rubber as the rubber raw material, carbon black or white carbon black as the reinforcing agent, and successively undergoing rubber mastication, kneading and vulcanization processes, among which rubber The mastication, mixing and vulcanization processes are carried out according to the usual process methods. But in order to realize the object of the present invention, in rubber mixing process, adopt silicon carbide fine powder to replace part reinforcing agent, and add silane coupling agent, rubber raw material, reinforcing agent, silicon carbide fine powder and silane coupling agent in rubber mixing process The ratio of parts by weight of the amount of coupling agent added is: 100 parts of rubber raw material, 20-45 parts of carbon black or white carbon black, 5-50 parts of silicon carbide micropowder, 0.4-2.45 parts of silane coupling agent, and the natural rubber is Standard rubber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rubber composition with low calorification and low rolling resistance. The rubber composition is prepared by successively carrying out plastification, mixing and vulcanization on rubber based on natural rubber as a rubber raw material and carbon black or white carbon black as a reinforcing agent; in the mixing process of the rubber, silicon carbide micropowder is adopted to replace partial reinforcing agent, a silane coupling agent is added, and the added amounts of the rubber material, the reinforcing agent, the silicon carbide micropowder and the silane coupling agent in the mixing process of the rubber are as follows in parts by weight: 100 part of rubber material, 20-45 parts of carbon black or white carbon black, 5-50 parts of silicon carbide micropowder and 0.4-2.45 parts of silane coupling agent; the silicon carbide micropowder is in an alpha or beta crystal form, and the particle diameter of the silicon carbide micropowder is 0..001mu m-50mu m. According to the invention, the processing performance of the mixed rubber is improved, the compression calorification of vulcanized rubber is reduced, the rolling resistance is obviously reduced, and the slip-wet resistance is improved.

Description

technical field [0001] The present invention relates to a rubber composition, particularly a rubber composition having low heat build-up and low rolling resistance. Background technique [0002] In order to improve the mechanical properties of the vulcanized rubber, carbon black needs to be added to the rubber composition as a reinforcing agent. The reinforcing agent can significantly increase the compression heat generation of the vulcanized rubber while improving the mechanical properties of the vulcanized rubber. Compression heat generation has a great influence on the performance of rubber products that need to be repeatedly deformed. If the compression heat generation is too large, the rubber product will heat up rapidly. The temperature rise not only accelerates the thermo-oxidative aging of rubber, but also may cause rubber products to deteriorate due to excessive temperature. destruction. Car tire blowout in summer driving is a typical example. In addition to selec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08K13/02C08K3/34C08K3/04C08K5/548
CPCY02T10/86
Inventor 孙毅曲丽伟李花婷王清才王玉东周志峰杨正宏张强宋中学
Owner PINGDINGSHAN YICHENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com