Circuit ceramic material composition and preparation process thereof

A line ceramic and formula technology, applied in the production of ceramic materials, clay products, other household appliances, etc., can solve the problems of consumption, shortage in Jiangsu and Zhejiang regions, and high formula cost, and achieve the effect of improving economic efficiency, reducing pollution and excellent performance.

Inactive Publication Date: 2013-09-11
贝爱达电器制造股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the current line porcelain material formulas are prepared in the form of genuine materials. Jiangsu and Zhejiang regions lack high-quality mineral resources, resulting in high cost of formulas; Contains a lot of mud particles, usually these sewage and mud particles are disposed of as garbage, and various types of energy are consumed during treatment, and various types of pollution must be strictly controlled to meet environmental protection requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Circuit ceramic material composition and preparation process thereof
  • Circuit ceramic material composition and preparation process thereof
  • Circuit ceramic material composition and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Electric porcelain sludge 500kg Guangdong white clay 280kg

[0017] Zuo Yun Clay 120kg Houxi Porcelain Clay 100kg

Embodiment 2

[0019] Electric porcelain sludge 490kg Guangdong white clay 260kg

[0020] Zuoyun Clay 140kg Houxi Porcelain Clay 110kg

Embodiment 3

[0022] Electric porcelain sludge 495kg Guangdong white clay 270kg

[0023] Zuoyun Clay 125kg Houxi Porcelain Clay 110kg

[0024] The percentages of the main mineral components of the electric porcelain sludge are as follows: 28.0% quartz, 16.9% kaolinite, 1.4% muscovite, 15.0% illite, 9.9% potassium feldspar, 12.9% pyrophyllite, and 15.2% corundum.

[0025] The main mineral components of Houxi porcelain clay are quartz, kaolin, illite and feldspar, and mainly contain the following components SiO 2 、Al 2 o 3 , Fe 2 o 3 、TiO 2 , MgO, CaO, K 2 O, Na 2 O, where SiO 2 、Al 2 o 3 and K 2 The percentages of O are 76%, 14%, and 4.5%, respectively.

[0026] First extract the electric ceramic sludge for standby, the steps are as follows: sewage→sewage treatment, purification→sludge slurry pressing→extraction for standby; and then complete the manufacture of line porcelain materials: batching→ball milling→squeezing mud→stale→sliming→forming→drying room Drying → kiln firing. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a circuit ceramic material composition which is made by recycling waste electroceramics. Currently, most ceramic material compositions are made of regular materials and high in cost as East China lacks of excellent mineral resources. The circuit ceramic material composition is made of, by weight, 4.5-5.0 parts of electroceramic sludge, 2.5-3.0 parts of Guangdong white sludge (Guangdong Qingcao mountain kaolin), 1.0-1.5 parts of Zuoyun clay and 1.0 part of Houxi china clay, wherein the main mineral components of the Houxi china clay include quartz, kaolin, illite and feldspar, and SiO2, AlO3 and K2O are 76%, 14% and 4.5% in percentage content respectively. Wastes are recycled and turned to be profitable, pollution caused by waste discharge is effectively reduced, energy conservation and environment protection are realized, economic benefit is further improved, and prepared electromagnetic materials are excellent in performance.

Description

technical field [0001] The invention relates to a line porcelain material formula, in particular to a line porcelain material formula made by reusing discarded electric porcelain sludge. Background technique [0002] Most of the current line porcelain material formulas are prepared in the form of genuine materials. Jiangsu and Zhejiang regions lack high-quality mineral resources, resulting in high cost of formulas; Contains more mud particles, usually these sewage and mud particles are disposed of as garbage, and various types of energy are consumed during treatment, and various types of pollution must be strictly controlled to meet environmental protection requirements. Contents of the invention [0003] Aiming at the defects in the prior art, the present invention provides a circuit ceramic material formula and its manufacturing process, which recycles discarded electric porcelain sludge, turns waste into wealth, reduces pollution, and generates new benefits. [0004] F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/132C04B33/24C04B33/26
CPCY02P40/60
Inventor 何汇洲徐彩霞徐素建
Owner 贝爱达电器制造股份有限公司