Composite cored wire for steelmaking and preparation method thereof

A technology of cored wire and steel shell, which is applied in the field of metallurgical steelmaking, can solve the problems affecting the purity of clean steel, and achieve the effects of reducing the probability of splashing, high desulfurization efficiency, and improving quality

Inactive Publication Date: 2014-07-30
秦皇岛双轮环保科技股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above several cored wires can meet the technical requirements of steel refining, but new problems have arisen. The impurities such as O, S, P, C, and Si in the molten steel are removed from the molten steel and entered into the slag. When the O, S, P, C, Si and other impurities in the steel slag reach a saturated state, some of them will return to the molten steel to affect the purity of the clean steel. This requires that the steel slag should also be removed while removing the impurities in the molten steel. Impurities in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The technology of the present invention provides a production method of refined steel solid core composite cored wire. The production method is to passivate the calcium ingot, then heat and soften it, extrude the calcium wire through an extruder, and then pass the refining The steel slow-release agent is crushed into powder, the calcium wire and the slow-release agent are wrapped with a steel belt by a wrapping machine, and the cored wire is wound into a coil by a winding machine, and finally sealed and packaged.

[0028] The parameters of composite cored wire are as follows:

[0029] 1. Core-spun wire diameter: 11-14mm.

[0030] 2. Core wire composition (wt%): steel shell 45; calcium wire 15; slow release agent 40.

[0031] 3. Weight per meter (g): steel shell 190; solid core calcium 55 and slow-release agent 165.

[0032] 4. The chemical composition of calcium wire is: Ca≥96wt%, Fe≤0.015wt%, Ni≤0.004wt%, Cu≤0.0025 wt%, Mg≤0.65 wt%, Al≤0.6 wt%, Si≤0.012 wt%, susta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite cored wire for steelmaking and a preparation method thereof, aiming to provide a deep slow-release deoxidation technology for clean steel and steelmaking, which can not only remove impurities in molten steel but also remove impurities in steel slag . According to a certain proportion of components and method steps, the composite cored wire prepared has high deoxidation and desulfurization efficiency, reduces the probability of calcium splashing, greatly improves the yield of calcium treatment, and reduces the cost of calcium treatment. It can effectively remove the oxygen in the steel slag, and prevent the oxygen in the steel slag from re-invading into the molten steel after being saturated.

Description

technical field [0001] The invention relates to the field of metallurgy and steelmaking, in particular to a composite cored wire for clean steelmaking and a preparation method thereof. Background technique [0002] At present, powder core cored wire and solid core pure calcium wire have been widely used in steel production, and the usage of refined steel cored wire exceeds 70%. [0003] In recent years, with the rapid development of my country's iron and steel industry, the proportion of low-carbon and low-silicon steel grades has increased. It is required to deoxidize, desulfurize, change the shape of inclusions, promote the floating of inclusions, purify molten steel, and improve the pourability of molten steel during calcium treatment. In addition to functions such as anti-corrosion properties, it is also required that no other substances be added to the molten steel, which will affect the purity of the clean steel. Since aluminum-calcium wire, silicon-calcium wire, etc. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/00
Inventor 姚博闻姚殿宝
Owner 秦皇岛双轮环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap