Thin strip steel for thin-wall oil drum and manufacturing method of thin strip steel

A manufacturing method and technology for thin strip steel, applied in the direction of metal rolling, etc., can solve the problems of low elongation, high yield ratio, poor formability, etc.

Active Publication Date: 2012-11-28
BAOSHAN IRON & STEEL CO LTD
View PDF15 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When thin strip continuous casting produces this kind of steel, it can solve the problems of uneven structure, low elongation, high yield strength ratio and poor formability in the thin strip continuous c...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thin strip steel for thin-wall oil drum and manufacturing method of thin strip steel
  • Thin strip steel for thin-wall oil drum and manufacturing method of thin strip steel
  • Thin strip steel for thin-wall oil drum and manufacturing method of thin strip steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0077] see figure 1 , the technological process of the present invention: the molten steel passes through the ladle 1, and is directly poured on a crystallization roller 5a, 5b and a side sealing plate which are rotated relatively and can be cooled rapidly through the ladle shroud 2, the tundish 3 and the flow distribution device 4 In the molten pool 7 surrounded by the devices 6a and 6b, the molten steel solidifies on the rotating circumferential surface of the crystallization rollers 5a and 5b, and then forms a solidified shell and gradually grows, and then forms a 1.5-3mm shell at the smallest gap (nip point) between the two crystallization rollers. Thick cast belt11. The casting strip passes through the secondary cooling device 8 in the airtight chamber 10, and immediately sprays dry ice (solid CO 2 ), to control the cooling rate, so that the casting belt 11 is rapidly and uniformly cooled to below 1280°C. Then the cast strip is sent to the hot rolling mill 13 by swingi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a thin strip steel for a thin-wall oil drum and a manufacturing method of the thin strip steel. Double-roll thin strip continuous production is adopted; a dry ice spray mode is adopted after a cast strip is discharged from a crystallization roll; uniform enhanced cooling is performed on the cast strip; the cast strip is quickly cooled to be below 1,280 DEG C; the cooling rate is 200-300 DEG C/s; in such a cooling mode, separation of coarse BN (Boron Nitride) can be promoted and low-melting-point phase B2O3 and fine AlN (Aluminum Nitride) separation are prevented to fulfill the aims of uniformizing austenite crystal grains and reducing the yield ratio; and then austenite is recrystallized and rolled on line, and the strip steel which is subjected to hot rolling is cooled through anti-oxidation quick cooling, wherein the cooling rate is 80-200 DEG C/s and the coiling temperature is 500-600 DEG C. Through the invention, the thin strip steel for the thin-wall oil drum with low yield ratio and superior impact performance can be obtained. According to the thin strip steel for the thin-wall oil drum produced by the method, the hot thin strip steel can be directly used in place of a cold one, a cold rolling step is removed, and the production cost is greatly reduced.

Description

technical field [0001] The invention relates to a continuous casting process, in particular to a thin steel strip for thin-walled oil barrels and a manufacturing method thereof. Background technique [0002] In the traditional steel production process, tin (Sn) is a typical residual element or harmful element in steel. It is very difficult and expensive to fully remove Sn in the steelmaking process. Once Sn is contained in steel, it is basically impossible to completely eliminate it. , can only reduce the content of Sn by diluting molten steel, all of which lead to the increase of the cost of steel products. [0003] In recent years, due to the continuous recycling of scrap steel, the content of residual elements such as Sn in steel has gradually increased. Sn in steel is an element that is easy to segregate, and it is easy to be enriched at the grain boundary to cause defects such as cracks. Therefore, in the traditional process The content of Sn element in steel is strict...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/04C22C33/04C21D8/02B21B1/46
Inventor 吴建春方园于艳
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap