Preparation method of stereoscopic low-carbon fur spun wool
A wool worsted and worsted spinning technology, which is applied in the field of textile fabrics, can solve the problems of high fabric finishing temperature, long production process cycle, and long process flow, etc., and achieve high yarn bulkiness, strong three-dimensional effect, and reduced twisting The effect of the number of times
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] The three-dimensional fabric is made by interlacing strands and single yarns. The strands and single yarns are worsted yarns, which are blended by wool and lyocell fibers. The yarn count of the worsted yarns is 2 strands. 78 public counts and 48 public counts per share, the blending ratio of the worsted yarns is: Paulai Fiber Paste 50wt%, wool 50wt%. The weaving is designed on a circular knitting machine with 5-6 small loops in the front (upper layer) transverse and longitudinal direction and the back (lower layer) long floating lines are assembled together to form a small pattern. In the finishing step, the liquid flow washing temperature Increase the temperature from 40°C to 100°C at a rate of 2°C / min and keep it for 55 minutes. The warp stitch density of the fabric is 245 pieces / 10cm, and the weft stitch density is 220 pieces / 10cm.
[0029] In this embodiment, the worsted yarn blended with wool and Paolai fiber, through special weaving and finishing, ...
Example Embodiment
[0030] Example 2
[0031] The three-dimensional fabric is made by interlacing strands and single yarns. The strands and single yarns are worsted yarns, which are blended by wool and lyocell fibers. The yarn count of the worsted yarns is 2 strands. 76 public counts and 1 share 46 public counts, and the blending ratio of the worsted yarns is: Paula Fiber Paste 45 wt.%, wool 55 Wt.%. The weaving is designed on a circular knitting machine with 8 coils in a reverse oblique chevron shape to form a wave shape. In the finishing step, the liquid flow scouring temperature is increased from 40°C to 110°C at 2°C / min, and the temperature is kept for 65 minutes. The warp stitch density of the fabric is 260 pieces / 10cm, and the weft stitch density is 230 pieces / 10cm.
[0032] In this embodiment, the worsted yarn blended with wool and Paolai fiber, through special weaving and finishing, the production process is reduced, the cycle is shortened, and the energy consumption is reduced, but the fabri...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap