Roasting system and roasting method for lithium-ore acidification by using externally-heated type rotary furnace

An external heating rotary furnace and acidification roasting technology, which is applied in lithium sulfate/sulfite, chemical industry, sustainable manufacturing/processing, etc., can solve the problems of difficult effective utilization, severe equipment corrosion, and large consumption of sulfuric acid, etc. problems, to achieve the effects of easy heat recovery, reduced emissions, and high heat exchange efficiency

Active Publication Date: 2014-03-19
西安三瑞超鼎新能源科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Lithium salt manufacturers at home and abroad mostly use internal heating rotary acidification roasting furnaces (kilns) to realize this process, which has the disadvantages of large sulfuric acid consumption, large tail gas volume, serious pollution, and serious equipment corrosion. Exhaust gas is taken away, it is difficult to realize effective utilization, and the energy consumption is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roasting system and roasting method for lithium-ore acidification by using externally-heated type rotary furnace
  • Roasting system and roasting method for lithium-ore acidification by using externally-heated type rotary furnace
  • Roasting system and roasting method for lithium-ore acidification by using externally-heated type rotary furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] 1) The β-spodumene is sent to the spodumene silo through the bucket elevator after being cooled and ground to 200 mesh after high-temperature transformation and roasting. The raw material composition is shown in the following table:

[0058] components

Li 2 o

SiO 2

al 2 o 3

P 2 o 5

K 2 o

Na 2 o

FeO

MgO

CaO

MnO

F

burn out

Content%

6.00

62.21

28.42

-

0.15

0.14

0.12

0.13

0.11

-

-

-

[0059] Note: "-" is an untested item, and its content is included in other impurities.

[0060] The discharge of the spodumene silo uses a pneumatic floatation system and a silo wall vibration device. After the spodumene in the silo is weighed and measured by the screw feeder, it enters the coulter type mixer;

[0061] 2) At the same time, the sulfuric acid used in acidification roasting is composed of concentrated sulfuric acid with ...

Embodiment 2

[0066]1) The β-spodumene raw material from the outside is sent into the spodumene silo, and the composition of the raw material is shown in the table below:

[0067] components

Li 2 o

SiO 2

al 2 o 3

P 2 o 5

K 2 o

Na 2 o

FeO

MgO

CaO

MnO

F

burn out

[0068] Content%

6.00

62.21

28.42

-

0.15

0.14

0.12

0.13

0.11

-

-

-

[0069] Note: "-" is an untested item, and its content is included in other impurities.

[0070] The arch-breaking screw is set in the silo, and the spodumene in the silo is weighed and measured by the belt scale, and then enters the gravity-free mixer to be mixed with sulfuric acid and then sent to the rotary acidification furnace. A stand-alone dust collector is installed on the top of the silo to remove the dust generated when the spodumene enters the silo and falls.

[0071] 2) At the same time, the su...

Embodiment 3

[0076] 1) The β-spodumene raw material from the outside is sent into the spodumene silo, and the composition of the raw material is shown in the table below:

[0077] components

Li 2 o

SiO 2

al 2 o 3

P 2 o 5

K 2 o

Na 2 o

FeO

MgO

CaO

MnO

F

burn out

Content%

6.00

64.76

27.72

-

-

0.22

0.32

0.16

-

-

-

-

[0078] Note: "-" is an untested item, and its content is included in other impurities.

[0079] The arch-breaking screw is set in the silo, and the spodumene in the silo is weighed and measured by the belt scale, and then enters the gravity-free mixer to be mixed with sulfuric acid and then sent to the rotary acidification furnace.

[0080] 2) At the same time, the sulfuric acid with a concentration of 98% is sent to the sulfuric acid absorption tower, and the fuming sulfuric acid with a concentration of 20% is sent to th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a roasting system and a roasting method for lithium-ore acidification by using an externally-heated type rotary furnace, which comprises the following steps of: generating acidifying grog through acidifying roasting after mixing beta lithium ores and sulfuric acid by using the externally-heated type rotary furnace as the core equipment of acidifying roasting reaction, and sending the acidifying grog which is generated after acidifying roasting into a subsequent working procedure after cooling the acidifying grog, wherein the sulfuric acid for acidifying roasting is used after the concentration of an acid liquor after tail gas is washed is adjusted through fuming sulfuric acid and can also be directly prepared from concentrated sulfuric acid or fuming acid or by mixing the two acids; the tail gas which is generated in the process of acidifying roasting is discharged with reaching standards after acid washing and alkali washing, and most of the acidic gas in the tail gas returns to the roasting system along with the washing acid to be reutilized during acid washing. The invention overcomes the defects of large tail-gas quantity, serious pollution and the like of a traditional internally-heated type acidifying-roasting process and provides a good method for the extraction of metallic lithium in the lithium ores, the self-heating of the reaction is fully utilized, energy does not need to be additionally consumed after the self reaction temperature is reached, and the energy-saving effect is remarkable.

Description

technical field [0001] The invention belongs to the technical field of lithium salt production, and relates to a system and method for acidifying and roasting lithium ore with an externally heated rotary furnace, specifically a system and method for sulfurating and roasting lithium ore with an externally heated rotary furnace as the core equipment . Background technique [0002] There are many ways to extract lithium from lithium ore, but the sulfuric acid method is still the most widely used lithium extraction method in the world. Most lithium salt manufacturers at home and abroad currently widely use this process. The sulfuric acid method has the advantages of small material flow and high production efficiency. , low energy consumption, high metal recovery rate and other outstanding advantages, so the lithium salt produced by this method accounts for a very high proportion of the world's total lithium salt production. [0003] Taking spodumene as an example, the principle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01D15/06
CPCY02P20/10
Inventor 何建祥魏超杨扬刘明会
Owner 西安三瑞超鼎新能源科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com