Phenyl-containing MT type resin and preparation method thereof

A resin and phenyl technology, applied in the field of phenyl-containing MT-type resin and its preparation, can solve the problems of different refractive index, white turbidity of compound liquid silicone rubber, etc. Effect

Active Publication Date: 2013-01-16
ZHONGHAO CHENGUANG RES INST OF CHEMICALINDUSTRY CO LTD
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the control of the molecular weight of synthetic MT-type resins is mainly controlled by different M / T ratios. Because MT resins with different M / T ratios have different phenyl content, there are differences in refractive index when compounding with different molecular weights. , and the difference in refractive index will cause white turbidity in the compound liquid silicone rubber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add 72g of deionized water, 250ml of toluene, 0.01g of concentrated sulfuric acid (concentration 98%) into a four-neck flask equipped with mechanical stirring, reflux condenser, thermometer and dropping funnel, raise the temperature to 60°C and add 42.3g of 1,3 - divinyl 1,1,3,3-tetramethyldisiloxane with 524.7 g of phenyltrimethoxysilane. After the dropwise addition, react at reflux temperature for 5 hours, cool, add 400 ml of toluene, neutralize to neutral with sodium bicarbonate, then add 1 ml of 30% acetic acid aqueous solution to acid, wash with water until neutral, and remove the solvent in vacuo , maintain a low boiling point at 190°C for 2 hours to remove small molecular impurities, and obtain a colorless and transparent vinyl phenyl MT resin with a weight-average molecular weight of 823 and a refractive index of 1.536 as measured by GPC.

Embodiment 2

[0025] Add 72g of deionized water, 250ml of toluene, 0.01g of concentrated sulfuric acid (concentration 98%) into a four-neck flask equipped with mechanical stirring, reflux condenser, thermometer and dropping funnel, raise the temperature to 80°C and add 37.4g of Hexamethasone dropwise phenyl disiloxane and 524.7g phenyltrimethoxysilane. After the dropwise addition, react at reflux temperature for 5 hours, cool, add 400 milliliters of toluene, neutralize to neutrality with sodium bicarbonate, then add 1 milliliter of 30% acetic acid aqueous solution to acidity, wash with water to neutrality, and remove the solvent in vacuo. Maintain low boiling at 190°C for 2 hours to remove small molecule impurities to obtain a colorless and transparent trimethylphenyl MT resin with a weight average molecular weight of 785 and a refractive index of 1.534 as measured by GPC.

Embodiment 3

[0027] Add 72g of deionized water, 250ml of toluene, and 0.13g of trifluoromethanesulfonic acid into a four-necked flask with mechanical stirring, reflux condenser, thermometer and dropping funnel, and add 22.9g of trimethylmethane dropwise at 90°C. Oxysilane and 52.88 g of phenyltriethoxysilane. After the dropwise addition, react at reflux temperature for 3 hours, cool, add 400 milliliters of toluene, neutralize to neutral with sodium bicarbonate, then add 1 milliliter of 30% acetic acid aqueous solution to acid, wash with water until neutral, vacuum desolventization, Maintain low boiling at 190°C for 2 hours to remove small molecule impurities to obtain a colorless and transparent vinyl phenyl MT resin with a weight-average molecular weight of 1300 and a refractive index of 1.536 as measured by GPC.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
refractive indexaaaaaaaaaa
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to phenyl-containing MT type resin and a preparation method thereof. The weight-average molecular weight of the phenyl-containing MT type resin is 800-8000. The preparation method of the phenyl-containing MT type resin includes the steps: (1) dissolving acid catalysts into solvent, increasing the temperature to 50-90 DEG C, dropwise adding a mixture of phenyl tri-alkoxy silane and monofunctional alkoxy silane and reacting for 3-8 hours; (2) decreasing the temperature of a reaction mixture to the room temperature, neutralizing the reaction mixture to neutrality, filtering and washing; and (3) removing the solvent so that the phenyl-containing MT type resin is obtained. The phenyl-containing MT type resin prepared by the method has the weight-average molecular weight of 800-8000 and can be applied to high-refraction liquid silicone rubber.

Description

technical field [0001] The invention relates to the field of silicone resins, in particular to a phenyl-containing MT-type resin and a preparation method thereof. Background technique [0002] MT-type resins refer to resins including trifunctional monomers (T units) and monofunctional monomers (M units). Phenyl-containing silicone liquid silica gel has excellent high and low temperature resistance, radiation resistance, wide operating temperature range, and high refractive index performance. It has a wide range of applications in various industries, especially aerospace, national defense, electronic and optical device packaging application. The phenyl-containing MT resin has an irreplaceable role as a reinforcing agent in transparent high-refractive liquid silicone rubber, and the combination of MT resins with different molecular weights has a better reinforcing effect on the mechanical properties of liquid silicone rubber. [0003] At present, the synthesis method of phen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/04C08G77/20C08G77/06
Inventor 涂世俭宋振虎李新莹张建新屈均
Owner ZHONGHAO CHENGUANG RES INST OF CHEMICALINDUSTRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com