Silicon vanadium nitride and production method thereof

A production method, silicon nitride vanadium alloy technology, applied in the field of ferroalloy preparation, can solve the problems of unstable yield rate, easy pulverization of products, etc., and achieve the effect of stable absorption rate and high absorption rate

Inactive Publication Date: 2013-01-23
LIAONING XINYE NEW MATERIAL
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The resulting product is easy to pulverize and the yield is unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicon vanadium nitride and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A silicon nitride vanadium alloy, which is composed of: 53.00 wt% vanadium, 13.00 wt% nitrogen, 6.86 wt% silicon, and the balance is iron and unavoidable impurities.

Embodiment 2

[0035] A silicon nitride vanadium alloy, which is composed of: 55.00 wt% vanadium, 15.00 wt% nitrogen, 9.89 wt% silicon, and the balance is iron and unavoidable impurities.

Embodiment 3

[0037] A silicon nitride vanadium alloy is composed of: 52.00 wt% vanadium, 13.00 wt% nitrogen, 7.58 wt% silicon, and the balance is iron and unavoidable impurities.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to silicon vanadium nitride which comprises the following components in percentage by weight: 52-55 wt percent of vanadium, 13-15 wt percent of nitrogen, 6-10 wt percent of silicon and the balance of iron and inevitable impurities, wherein the mass ratio of vanadium to nitrogen is 3.6-4.5. A silicon vanadium nitride alloy can be prepared through high-temperature self-propagating reaction. According to the silicon vanadium nitride alloy disclosed by the invention, by adding the element silicon in the alloy, controlling the element silicon content in the alloy and controlling the contents of vanadium and nitrogen as major elements and the ratio of vanadium and nitrogen, the absorptivity and the stability of the silicon vanadium nitride alloy are greatly improved; and in addition, the silicon vanadium nitride alloy is a vanadium microalloy in most vanadium saving at present and has excellent market competitiveness.

Description

technical field [0001] The invention belongs to the technical field of ferroalloy preparation, and more specifically, the invention relates to a silicon vanadium nitride and a production method thereof. Background technique [0002] The alloying of steel is usually based on manganese and silicon; microalloys refer to ferroalloys that add trace carbon and nitrogen forming elements such as niobium, vanadium, and titanium on the basis of the main ferroalloy, and are widely used in the production of high-strength steel bars and low-strength steel bars. Alloy high-strength steel, pipeline steel, H-beam, medium and heavy plate, etc. [0003] Microalloys generally have the following characteristics: (1) The added carbonitride-forming elements strengthen the mechanical properties of steel through the "dissolution-precipitation" behavior during the heating and cooling process of steel; The mechanism is mainly fine grain strengthening and precipitation strengthening; (3) Microalloyin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C29/00C22C1/00C22C35/00
Inventor 谭国臣张光德于成智
Owner LIAONING XINYE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com