Preparation method of vanadyl sulfate

A technology of vanadyl sulfate and sulfuric acid, which is applied in chemical instruments and methods, vanadium compounds, inorganic chemistry, etc., and can solve the problems of low dry basis content and insufficient purity of vanadyl sulfate products

Active Publication Date: 2013-03-06
PANGANG GROUP VANADIUM TITANIUM & RESOURCES +1
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But test result proves, in the vanadyl sulfate product that above-mentioned method obtains, the dry basis content of vanadyl sulfate is low, only 82% by weight, so the purity of the vanadyl sulfate product that this method obtains is not high enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0012] The invention provides a preparation method of vanadyl sulfate, which comprises the following steps: (1) dissolving vanadium pentoxide with sulfuric acid to obtain an activation solution; (2) contacting the activation solution with a reducing agent so that the The pentavalent vanadium in the activation solution is reduced to tetravalent vanadium to obtain a reduction product; (3) adjusting the pH value of the reduction product with an alkali, so that the tetravalent vanadium in the reduction product is separated out as a precipitate; (4) Dissolving the precipitate with sulfuric acid is used for crystallization to obtain vanadyl sulfate solid, and relative to 1 mole of tetravalent vanadium in the precipitate, the sulfuric acid is used in an amount of 0.9-1.1 moles.

[0013] Wherein, vanadium pentoxide can be obtained by methods known in the art, for example, by heating and decomposing ammonium vanadate, or can be obtained commercially. After vanadium pentoxide is dissolv...

Embodiment approach

[0031] According to a particularly preferred embodiment of the present invention, the method of the present invention comprises the following steps:

[0032] (1) dissolving vanadium pentoxide with 40-60% by weight of sulfuric acid aqueous solution under boiling conditions for 30-100 minutes to obtain an activated solution; the molar ratio of the sulfuric acid to vanadium pentoxide is 1: 0.15-0.2;

[0033] Diluting the activation solution with water, relative to each gram of vanadium pentoxide used to form the activation solution, the amount of water used for dilution is 5-15ml;

[0034] (2) at 50-70°C, contacting the diluted activation solution with excess sulfur dioxide for 30-80 minutes, so that the pentavalent vanadium in the activation solution is reduced to tetravalent vanadium to obtain a reduced product;

[0035] (3) adjust the pH value of the reduction product with sodium hydroxide to 4-6, preferably 4.5-5.5, more preferably 5-5.5, so that the tetravalent vanadium in t...

Embodiment 1

[0043] This example is used to illustrate the method provided by the present invention.

[0044] In the vanadium pentoxide of 100g (purchased from the Vanadium Products Factory of Pangang Iron and Steel Vanadium Titanium Co., Ltd., the purity is greater than 99.5% by weight), adding 634g concentration is the sulfuric acid aqueous solution of 50% by weight (the mol ratio of sulfuric acid and vanadium pentoxide About 1:0.17), then heated to boiling, and maintained under boiling conditions for 60 minutes to obtain an activated solution.

[0045] The above activated solution was cooled to room temperature, and then 1000 ml of water was added thereto for dilution.

[0046] At 60° C., in the diluted activation solution, an excessive amount of sulfur dioxide gas (purity greater than 99% by volume, and an amount of introduction greater than 0.6 mole) is passed into the diluted activation solution for 60 minutes, so that the pentavalent vanadium in the activation solution is reduced to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of vanadyl sulfate, which comprises the following steps: (1) dissolving vanadium pentoxide with sulfuric acid to obtain an activated solution; (2) contacting the activated solution with a reducing agent to reduce pentavalent vanadium in the activated solution into tetravalent vanadium so as to obtain a reduction product; (3) adjusting the pH value of the reduction product by an alkali to precipitate the tetravalent vanadium in the reduction product so as to obtain a precipitate; (4) dissolving the precipitate with sulfuric acid, performing crystallization to obtain a vanadyl sulfate solid, wherein with respect to 1 mole of tetravalent vanadium in the precipitate, the using amount of the sulfuric acid is 0.9-1.1 moles. The vanadyl sulfate product prepared by the method provided by the invention has a dry basis content of up to 97 wt%.

Description

technical field [0001] The invention relates to a preparation method of an inorganic compound, in particular to a preparation method of vanadyl sulfate. Background technique [0002] Vanadyl sulfate is also called vanadyl sulfate, and its chemical formula is VOSO 4 . Vanadyl sulfate has a wide range of uses, such as mordant, colorant, catalyst, battery electrolyte and medicine. In recent years, with the development of related industries, the demand for vanadyl sulfate is increasing year by year. [0003] Vanadyl sulfate is mainly prepared by reducing pentavalent vanadium to vanadyl ions containing tetravalent vanadium and crystallizing together with sulfate ions. For example, the document CN 101920994A discloses a preparation method of vanadyl sulfate: calcining ammonium metavanadate at a temperature of 540°C-600°C in a closed reactor; adding sulfuric acid to the calcined product and introducing SO 2 The gas is heated and boiled; the solution obtained after heating and b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G31/00
Inventor 胡力邓孝伯李千文常智魏朝辉
Owner PANGANG GROUP VANADIUM TITANIUM & RESOURCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com